Polymer Property : Cure Time = 5.00 hour Product List
Processing PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 300 - 360 min | 5.00 - 6.00 hour | 5 to 6 hours to send at 77°F. |
| Fibre Glast 1100 Light-Weight High-Strength Patching/Filler Compound Product Features:Very Light Weight MaterialNon-Hazardous Product - Safe to UseEasily Sanded and Carved with Shop ToolsNegligible ShrinkageNon-Critical, 2 to 1 Ratio by Weight or by VolumeExcellent N.. |
|||
| Cure Time | >= 300 min @Temperature 25.0 °C |
>= 5.00 hour @Temperature 77.0 °F |
|
| Lord Adhesives Aeroglaze® 9741 Epoxy Primer/Tie-Coat Aeroglaze® 9741 is a two-part epoxy primer designed for use on aluminum, metal, and prepared composite surfaces. Aeroglaze 9741 primer/tie-coat is applied to scuff-sanded urethane top coats and e.. |
|||
| Cure Time | >= 300 min @Temperature 25.0 °C |
>= 5.00 hour @Temperature 77.0 °F |
|
| Lord Adhesives Aeroglaze® 9743 Epoxy Primer/Tie-Coat Aeroglaze® 9743 is a two-part epoxy primer designed for use on aluminum, metal, and prepared composite surfaces. Aeroglaze 9743 primer/tie-coat can be applied to scuff-sanded urethane top coats a.. |
|||
| Cure Time | >= 300 min @Temperature 25.0 °C |
>= 5.00 hour @Temperature 77.0 °F |
|
| Lord Adhesives Aeroglaze® 9744 Epoxy Primer/Tie-Coat Aeroglaze® 9744 is a two-part epoxy primer designed for use on aluminum, metal, and prepared composite surfaces. Aeroglaze 9744 primer/tie-coat is applied to scuff-sanded urethane top coats and e.. |
|||
| Cure Time | 300 min | 5.00 hour | Fixture time |
| ITW Devcon Epoxy HP 250, Straw Information provided by ITW Devcon |
|||
| Cure Time | 300 min @Temperature 23.0 °C |
5.00 hour @Temperature 73.4 °F |
|
| Shin-Etsu Silicones KE-1052D A/b Silicone, Gel RTV Information Provided by Shin-Etsu Silicones of America, Inc. |
|||
| Cure Time | 300 min @Temperature 204 °C |
5.00 hour @Temperature 400 °F |
Recommended Post Cure Cycle |
| Arlon 51576XC15A 0.015" Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave: 3 mil PolyethyleneSide 2: Uncured Silicone RubberSubstrate: Style 7628 FiberglassSide 1: Cured Silicone RubberThis data represents typical values for the producti.. |
|||
| Cure Time | 300 min | 5.00 hour | Tack-Free Time |
| 3M AC-251 Black Class B-1 Aerospace Sealant 3M Aerospace Sealant AC-251 Black Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate ai.. |
|||
| Cure Time | 300 min | 5.00 hour | Tack-Free Time |
| 3M AC-350 Class A-1 Aerospace Sealant 3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have.. |
|||
| Cure Time | 300 - 360 min | 5.00 - 6.00 hour | |
| 3M AC-770 Class B-1 Aerospace Sealant 3M Aerospace Sealant AC-770 Class B are fast cure, low density two-component, manganese dioxide cure, polysulfide fuselage sealants. 3M AC-770 Class B Sealants have outstanding resistance to aviatio.. |
|||
| Cure Time | 300 min | 5.00 hour | Full Mechanical |
| 3M Scotchkote™ FG 512 Epoxy Ceramic Surfacer Scotchkote Epoxy Ceramic Surfacer FG 512 has been specifically developed as a ceramic enhanced epoxy repair coating for resurfacing and reforming metal machinery and equipment, such as pumps, impell.. |
|||
| Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
| Aremco Ceramacast™ 576-N High Temperature Potting & Casting Alumina Medium grain castable ceramic for large high temperature potting and tooling. Aremco offers a range of ceramic-based materials used for the assembly of high temperature, high power electrical devic.. |
|||
| Cure Time | 300 min | 5.00 hour | 2 hrs at 200°F; 3 hrs at 250°F |
| Aremco Ceramacast™ 584 High Temperature Potting & Casting Material Magnesia Two-part, quick-set ceramic for small parts. |
|||
| Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
| Aremco Ceramacast™ 586 High Temperature Potting & Casting Material Zirconia Silicate Castable ceramic for ceramic and metal assemblies. Excellent handling, fast curing. |
|||
| Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
| Aremco Ceramacast™ 645-N High Temperature Potting & Casting Material Silica Castable ceramic with low thermal conductivity. |
|||
| Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
| Aremco Ceramacast™ 673-N High Temperature Potting & Casting Material Silicon Carbide Single-part castable ceramic exhibiting high strength and thermal conductivity. |
|||
| Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
| Aremco Ceramacast™ 675 High Temperature Potting & Casting Material Aluminum Nitride Fine grain aluminum nitride castable with high thermal conductivity |
|||
| Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
| Aremco Ceramacast™ 675-N High Temperature Potting & Casting Material Aluminum Nitride Fine grain aluminum nitride castable with high thermal conductivity. |
|||
| Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
| Aremco Ceramacast™ 895 High Temperature Potting & Casting Material Alumina Fine grain castable ceramic. |
|||
| Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
| Aremco Ceramacast™ 900 High Temperature Potting & Casting Material Zirconia Silicate High Density, high strength molding compound. |
|||
| Cure Time | 300 min | 5.00 hour | Time to Handling Strength |
| 3M Scotch-Weld™ LSB60 Toughened Epoxy Adhesives 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LBS60 is a high performance, two-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of f.. |
|||
| Cure Time | 300 min | 5.00 hour | Time to Handling Strength |
| 3M Scotch-Weld™ LSB60NS Toughened Epoxy Adhesives 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LBS60NS is a high performance, two-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of.. |
|||
| Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs Air Set; 3 hrs at 200°F |
| Aremco Pyro-Putty™ 2500 High Temperature Ceramic-Metallic Putty, Iron Oxide Filled Ceramic and Black Iron Oxide-Filled, One-Part, Water Based Paste.For Applications to 1/4" Thick.Repairs Cast Iron, and Steel Parts to 1600°F |
|||