Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 3.00 - 5.00 min @Thickness 6.35 mm, Temperature 149 °C |
0.0500 - 0.0833 hour @Thickness 0.250 in, Temperature 300 °F |
|
Quantum Composites QC-8777 41% Glass Fiber Reinforced Polyester Hybrid SMC QC-8777 is a polyester hybrid engineered structural composite molding compound designed for compression molding of components requiring high structural strength, corrosion resistance and temperature.. |
|||
Cure Time | 3.00 min | 0.0500 hour | |
Resin Technology Group 405 Oxy-Bond™ Electrically Conductive Epoxy Adhesive Oxy-Bond and Millenium Adhesive SystemsEngineered for strength, durability, lightness, and formability, our Oxy-Bond and Millenium lines offer adhesives with physical and electrical properties to ma.. |
|||
Cure Time | <= 3.00 min | <= 0.0500 hour | Induction |
Permabond ES578 Epoxy Resin PERMABOND® ES578 is a single-part heat cured epoxy adhesive with excellent adhesion to metal surfaces, ceramics as well as composite materials. ES578 provides excellent thermal conductivity and bon.. |
|||
Cure Time | 3.00 - 43200 min | 0.0500 - 720 hour | Average value: 4860 min Grade Count:57 |
Overview of materials for Thermoset Polyurethane, Adhesive This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Adhesive". Each property range of values reported is minimum and maximum values .. |
|||
Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 350ºF Cure Temperature MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Cure Time | <= 3.00 min | <= 0.0500 hour | Induction |
Permabond ES569 Epoxy Resin PERMABOND® ES569 is a single-part heat cured epoxy adhesive with excellent adhesion to metal surfaces as well as composite materials. The high bond strength of this adhesive allows it to replace me.. |
|||
Cure Time | 3.00 - 5.00 min | 0.0500 - 0.0833 hour | handling time |
Permabond TA4302 Toughened Acrylic Adhesive PERMABOND® TA4302 is a 2-part, 1:1 toughened acrylic adhesive. It can be used to bond a wide variety of materials including metals, plastics, GRP, ceramics, wood and other substrates. It is conveni.. |
|||
Cure Time | 3.00 - 5.00 min | 0.0500 - 0.0833 hour | Working time |
ITW Devcon Flex Welderâ„¢ Methacrylate Adhesive FC, Off-White, Black Information provided by ITW Devcon |
|||
Cure Time | 3.00 min @Temperature 88.0 °C |
0.0500 hour @Temperature 190 °F |
|
Lord Adhesives Chemlok® 144 Primer LORD Chemlok® 144 primer is a one-coat, moisturecure primer used to prime and/or bond a variety of polar substrates. These substrates include steel, aluminum, brass, e-coated metal, glass fabric,.. |
|||
Cure Time | 3.00 min | 0.0500 hour | Tack Free Time |
Shin-Etsu Silicones KE-3490 Silicone, RTV Information Provided by Shin-Etsu Silicones of America, Inc. |
|||
Cure Time | 3.00 min | 0.0500 hour | Tack Free Time |
Shin-Etsu Silicones KE-3493 Silicone, RTV Information Provided by Shin-Etsu Silicones of America, Inc. |
|||
Cure Time | >= 3.00 min | >= 0.0500 hour | |
Trelleborg Emerson & Cuming Stycast® A-312 One-Component General Purpose Encapsulant Features and Typical Applications: Designed as general purpose encapsulants, these products offer a wide range of features including thermal conductivity, mechanical shock and impact resistance, as .. |
|||
Cure Time | 3.00 min | 0.0500 hour | |
Loctite® 3273 Acrylic Bonding Adhesive Acrylic Bonding AdhesivesLoctite® Acrylic Adhesives were developed for bonding applications that require tensile, shear and peel strength combined with maximum impact, stress and shock resistance. .. |
|||
Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 350ºF Cure Temperature MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 76A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 83A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Cure Time | 3.00 min | 0.0500 hour | Curelastmeter |
Daikin DAI-EL G-704 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content Offers minimal compression set and excellent sealing. The copolymer type offers good compression set characteristics.Information provided by Daikin Industries. |
|||
Cure Time | 3.00 min | 0.0500 hour | Curelastmeter |
Daikin DAI-EL G-901 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 71% Fluorine Content Offers excellent chemical and steam resistance. Offers good mechanical characteristics.Features: Excellent solvent resistance.Information provided by Daikin Industries. |
|||
Cure Time | 3.00 - 5.00 min | 0.0500 - 0.0833 hour | Open Time |
3M 5010 Polyurethane Multi-Purpose Adhesive 3M™ Polyurethane Multi-Purpose Adhesive 5010 is a one component, fast curing adhesive which forms a rigid permanent bond. 3M 5010 bonds to a wide variety of materials including wood, foam panels, f.. |
|||
Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 76A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 83A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Cure Time | 3.00 min | 0.0500 hour | 6 min. @ 130ºC, 3 min. @ 150ºC |
Loctite® 3889 Rapid Cure Isotropic Epoxy Adhesive Electrically Conductive BondersLoctite® Electrically Conductive Adhesives are used in a variety of applications where electrical connectivity is needed, providing a conductive path where traditiona.. |
|||
Cure Time | 3.00 - 5.00 min @Temperature 138 - 138 °C |
0.0500 - 0.0833 hour @Temperature 280 - 280 °F |
Average value: 5.17 min Grade Count:1 |
Overview of materials for Vinyl Ester Sheet Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Vinyl Ester Sheet Molding Compound". Each property range of values reported is minimum and maximum value.. |
|||
Cure Time | 3.00 - 5.00 min @Thickness 6.35 - 6.35 mm |
0.0500 - 0.0833 hour @Thickness 0.250 - 0.250 in |
Average value: 5.17 min Grade Count:1 |
Overview of materials for Vinyl Ester Sheet Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Vinyl Ester Sheet Molding Compound". Each property range of values reported is minimum and maximum value.. |
|||
Cure Time | 3.00 min @Temperature 204 °C |
0.0500 hour @Temperature 400 °F |
|
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 65A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Cure Time | 3.00 min | 0.0500 hour | 10 min. @ 125ºC, 6 min. @ 150ºC, 3 min. @ 175ºC |
Loctite® 3880 Heat Cure Isotropic Epoxy Adhesive Electrically Conductive BondersLoctite® Electrically Conductive Adhesives are used in a variety of applications where electrical connectivity is needed, providing a conductive path where traditiona.. |