- Daikin DAI-EL G-704 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content
Daikin DAI-EL G-704 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Daikin Industries |
| Trade Name | DAI-EL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Daikin DAI-EL G-704 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Offers minimal compression set and excellent sealing. The copolymer type offers good compression set characteristics.Information provided by Daikin Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | at 25°C |
| Mooney Viscosity | 25 @Temperature 121 °C |
25 @Temperature 250 °F |
ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 72 | 72 | Peak value, at 25°C |
| Tensile Strength at Break | 12.7 MPa | 1840 psi | |
| Tensile Strength, Yield | 3.40 MPa @Strain 100 % |
493 psi @Strain 100 % |
|
| Elongation at Break | 230 % | 230 % | |
| Tear Strength | 21.6 kN/m | 123 pli | at 25°C |
| Compression Set | 15 % | 15 % | 70 hours at 25°C |
| 9.0 % @Temperature 100 °C |
9.0 % @Temperature 212 °F |
70 hours | |
| 12 % @Temperature 175 °C |
12 % @Temperature 347 °F |
70 hours | |
| 22 % @Temperature 200 °C |
22 % @Temperature 392 °F |
70 hours |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Minimum Service Temperature, Air | -18.0 °C | -0.400 °F | TR test, TR10 |
| -14.5 °C | 5.90 °F | Gehman torsion test, T10 | |
| -8.00 °C | 17.6 °F | Gehman torsion test, T2 | |
| -8.00 °C | 17.6 °F | TR test, TR70 | |
| Brittleness Temperature | -21.0 °C | -5.80 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 170 °C | 338 °F | Cure Measuring Temperature |
| Cure Time | 3.00 min | 0.0500 hour | Curelastmeter |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP FARADEX KS002E Acetal Copolymer (Europe-Africa-Middle East)
- Resinlab® EP950NMF Gray Non-Metallic Filled Rubber Modified Epoxy
- Kinlead LSD12 Low Temperature Grade Heat Sealable Film (thickness: 18 µm)
- Iran Petrochemical (PCC) EP-N31MA Polypropylene
- Momentive Performance Materials HBR Hot-Pressed Boron Nitride
- A. Schulman POLYBATCH™ White LL8970 TS Concentrate Based In LLDPE
- Dow Corning 749 Fluid
- DSM Akulon® K240-HP (Dry) Impact Modified Nylon 6 (North America)
- DuPont Performance Polymers Crastin® CE15315 BK010 Polybutylene Terephthalate (PBT) (Unverified Data**)&l
- ExxonMobil LLDPE LL 3201.36 Linear Low Density Polyethylene Resin
Copyright © lookpolymers.com All Rights Reserved