Thermal Properties | Metric | English | Comments |
---|---|---|---|
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2025°F (1107°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 316°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 760°C (1400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, all-weld metal, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, all-weld metal, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Ultimet® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 23.0 °C |
0.112 BTU/lb-°F @Temperature 73.4 °F |
|
Carpenter BioDur™ CCM® Medical Implant Alloy, Annealed Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur Carpenter CCM alloy.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 23.0 °C |
0.112 BTU/lb-°F @Temperature 73.4 °F |
|
Carpenter BioDur™ CCM® Medical Implant Alloy, Warm Worked Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur Carpenter CCM alloy.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Sheet, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 23.0 °C |
0.112 BTU/lb-°F @Temperature 73.4 °F |
|
Carpenter BioDur™ CCM® Medical Implant Alloy, Hot Worked Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur Carpenter CCM alloy.. |
|||
Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Bar, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |