Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 13.6 W/m-K @Temperature 260 °C |
94.4 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 13.6 W/m-K @Temperature 260 °C |
94.4 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 13.6 W/m-K @Temperature 260 °C |
94.4 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 13.6 W/m-K @Temperature 260 °C |
94.4 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 13.6 W/m-K @Temperature 260 °C |
94.4 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 13.6 W/m-K @Temperature 260 °C |
94.4 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1121°C, air cooled, aged 16 hours at 899°C Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 13.6 W/m-K @Temperature 260 °C |
94.4 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include .. |