Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 21.1 W/m-K @Temperature 600 °C |
146 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 600 °C |
146 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 600 °C |
146 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 600 °C |
146 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 600 °C |
146 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 600 °C |
146 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 600 °C |
146 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 600 °C |
146 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 188 alloy, plate at RT after 4000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 600 °C |
146 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 500 °C |
146 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 214® alloy, 20% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 500 °C |
146 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 214® alloy, 20% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 500 °C |
146 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 214® alloy, 30% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 500 °C |
146 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 214® alloy, 40% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 500 °C |
146 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 214® alloy, 40% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 500 °C |
146 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 214® alloy, 50% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 500 °C |
146 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 214® alloy, 50% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 500 °C |
146 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 214® alloy, 50% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 500 °C |
146 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 214® alloy, sheet, 100 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 500 °C |
146 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 214® alloy, sheet, 1000 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 500 °C |
146 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 214® alloy, sheet, 1000 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 500 °C |
146 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 214® alloy, sheet, 32 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 500 °C |
146 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 214® alloy, sheet, 32 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 21.0 W/m-K @Temperature 85.0 °C |
146 BTU-in/hr-ft²-°F @Temperature 185 °F |
|
Indium Corp. Indalloy 11 Lead Solder Alloy Information Provided by Indium Corporation |
|||
Thermal Conductivity | 21.0 W/m-K @Temperature 20.0 °C |
146 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
Industeel TENASTEEL® Cold Work Tool Steel Description: TENASTEEL is a cold work tool steel, combining a high wear resistance together with a very high toughness. Its other advantages are a good machinability in the as-delivery condition and.. |
|||
Thermal Conductivity | 21.1 W/m-K @Temperature 500 °C |
146 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 214® alloy, 30% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 21.0 W/m-K | 146 BTU-in/hr-ft²-°F | |
California Fine Wire Nico Copper Nickel Resistance Wire All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
Thermal Conductivity | 21.0 W/m-K | 146 BTU-in/hr-ft²-°F | |
China-Yixing Longly Refractories 95 Alumina Ceramic Tubes & Rods LONGLY's alumina ceramic tubes and rods (the tolerances of +/- 0.02mm could be reached by mechanical or electronic finishing or mirror surface finishing) have high hardness, wear resistance, insulat.. |
|||
Thermal Conductivity | 21.0 W/m-K | 146 BTU-in/hr-ft²-°F | |
CeramTec 965 Toughened Alumina (Al2O3-ZrO2) Hasselman Thermal Shock value is 270 K.Data provided by CeramTec North America. |
|||
Thermal Conductivity | 21.0 W/m-K | 146 BTU-in/hr-ft²-°F | |
CeramTec SL200B Silicon Nitride SL200B ceramic material was designed especially for use in the field of welding technology. SL200B is a 100 bar gas-pressure sintered silicon nitride (Si3N4) with impressive properties. It boasts de.. |