Polymer Property : Thermal Conductivity = 137 BTU-in/hr-ftÂ²-Â°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English
Thermal Conductivity	19.7 W/m-K @Temperature 500 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes 263Â® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, 10% cold reduction, 1010Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, 20% cold reduction, 1065Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, 20% cold reduction, 1120Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, 30% cold reduction, 1065Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, 30% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, 40% cold reduction, 1065Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, 40% cold reduction, 1120Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, 40% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, 50% cold reduction, 1010Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, 50% cold reduction, 1065Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, 50% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, hot rolled and 1050Â°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, plate after 1000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, plate after 1000 hours at 760Â°C (1400Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, plate after 1000 hours at 870Â°C (1600Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, plate after 16000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, plate after 16000 hours at 870Â°C (1600Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, plate after 4000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, plate after 4000 hours at 760Â°C (1400Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, plate after 8000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 Â°C	137 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 625 alloy, plate, as annealed at 1025Â°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	19.8 W/m-K @Temperature 700 °C	137 BTU-in/hr-ft²-°F @Temperature 1290 °F
Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Thermal Conductivity	19.8 W/m-K @Temperature 700 °C	137 BTU-in/hr-ft²-°F @Temperature 1290 °F
Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Thermal Conductivity	19.8 W/m-K @Temperature 700 °C	137 BTU-in/hr-ft²-°F @Temperature 1290 °F
Haynes 625 alloy, 50% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Thermal Conductivity	19.8 W/m-K @Temperature 700 °C	137 BTU-in/hr-ft²-°F @Temperature 1290 °F
Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Thermal Conductivity	19.8 W/m-K @Temperature 700 °C	137 BTU-in/hr-ft²-°F @Temperature 1290 °F
Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var..
Thermal Conductivity	19.8 W/m-K @Temperature 700 °C	137 BTU-in/hr-ft²-°F @Temperature 1290 °F
Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Thermal Conductivity	19.8 W/m-K @Temperature 700 °C	137 BTU-in/hr-ft²-°F @Temperature 1290 °F
Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..