Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, 20% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, plate after 1000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, plate after 4000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, plate after 8000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 15.3 W/m-K | 106 BTU-in/hr-ft²-°F | |
Latrobe CSS-42L™ VIM-VAR High Performance Carburizing Stainless Steel; Bearing and Gear Steel CSS-42L™ is a case carburizable stainless steel alloy intended to be used at operating temperatures up to 800°F (427°C). The alloy is able to achieve and maintain a high surface hardness .. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 20.0 °C |
106 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
Schmolz + Bickenbach UGIMA 303 UX® Stainless Steel Bar Description: 303 UGIMA UX® is an improved machining grade produced only by Ugitech, providing the ultimate level of machinability available in an austenitic stainless steel. 303 UGIMA UX® feat.. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 20.0 °C |
106 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
Schmolz + Bickenbach UGIMA® 303 Stainless Steel Bar Description: 303 UGIMA® is Ugitech’s improved machining grade produced only by Ugitech. It is identical in every way to regular 303, except with respect to machinability. 303 UGIMA® repre.. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 20.0 °C |
106 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
Schmolz + Bickenbach UGIMA® 316/316L Stainless Steel Bar Description: 316/316L UGIMA® is Ugitech’s improved machining grade produced only by Ugitech. It is identical in every way to regular 316L, except with respect to machinability. 316/316L UGIM.. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Thermal Conductivity | 15.3 W/m-K @Temperature 400 °C |
106 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |