Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 40.0 - 60.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.2 - 33.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
SABIC Innovative Plastics Cycoloy® MC5210 PC+ABS (Asia Pacific) |
|||
CTE, linear | 50.0 - 60.0 µm/m-°C @Temperature 50.0 - 100 °C |
27.8 - 33.3 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group 6501 DAIP Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi.. |
|||
CTE, linear | 50.0 - 60.0 µm/m-°C @Temperature 50.0 - 100 °C |
27.8 - 33.3 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group 6552 DAIP Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi.. |
|||
CTE, linear | 5.00 - 60.0 µm/m-°C @Temperature 50.0 - 100 °C |
2.78 - 33.3 µin/in-°F @Temperature 122 - 212 °F |
Average value: 31.3 µm/m-°C Grade Count:8 |
Overview of materials for Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled". Each property range of values repor.. |
|||
CTE, linear | 40.0 - 60.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.2 - 33.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
SABIC Innovative Plastics Lexan® SP7602 PC (Asia Pacific) |
|||
CTE, linear | 30.6 - 60.0 µm/m-°C | 17.0 - 33.3 µin/in-°F | Average value: 44.1 µm/m-°C Grade Count:5 |
Overview of materials for Nylon 66, 10% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 10% Mineral Filled". Specific grades with primary filler content between 5% and 14% are includ.. |
|||
CTE, linear | 40.0 - 60.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.2 - 33.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
SABIC Innovative Plastics LNP THERMOCOMP Lexan_SP7602 PC (Asia Pacific) |
|||
CTE, linear | 40.0 - 60.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.2 - 33.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
SABIC Innovative Plastics Noryl GTX GTX870 PPE+PA6 (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
CTE, linear | 40.0 - 60.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.2 - 33.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
SABIC Innovative Plastics NORYL GTX GTX870 PPE+PA6 (Asia Pacific) |
|||
CTE, linear | 40.0 - 60.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.2 - 33.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
SABIC Innovative Plastics NORYL GTX870 PPE+PA6 (Asia Pacific) |
|||
CTE, linear | 55.0 - 60.0 µm/m-°C | 30.6 - 33.3 µin/in-°F | |
Master Bond UV15LV One Component, UV Curable Epoxy Based System Product Description: Master Bond UV15LV is a high strength, low viscosity, epoxy based UV curable system for bonding, sealing and coating. It has low viscosity and it is widely used in a variety of .. |
|||
CTE, linear | 55.0 - 60.0 µm/m-°C | 30.6 - 33.3 µin/in-°F | |
Hippe PEI A material with very high mechanical strength and high thermoforming stability which can be used at high temperatures. Distinguished by constant dielectric properties, a wide range of frequency and .. |
|||
CTE, linear | 50.0 - 60.0 µm/m-°C | 27.8 - 33.3 µin/in-°F | Average value: 51.8 µm/m-°C Grade Count:11 |
Overview of materials for Polyphenylene Sulfide (PPS), Unreinforced, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Unreinforced, Extruded". Each property range of values reported is minimum .. |