Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 30.0 - 35.0 µm/m-°C | 16.7 - 19.4 µin/in-°F | Polykemi |
Polykemi AB POLYblend 45FS GF20 PC/ABS-Blend, Glass Fiber reinforced Information provided by Polykemi AB |
|||
CTE, linear | 15.0 - 35.0 µm/m-°C @Temperature 50.0 - 100 °C |
8.33 - 19.4 µin/in-°F @Temperature 122 - 212 °F |
longitudinal; ISO 11359-2 |
Raschig Group MELOPLAS® 150 MF Wood flour-reinforced MF molding compound in dark colors. High surface hardness, high mechanical strength, good electrical properties. Self-extinguishing (V-O/1,6 according to UL 94), UL-listed. Fr.. |
|||
CTE, linear | 15.0 - 35.0 µm/m-°C @Temperature 50.0 - 100 °C |
8.33 - 19.4 µin/in-°F @Temperature 122 - 212 °F |
longitudinal; ISO 11359-2 |
Raschig Group MELOPLAS® 152 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
CTE, linear | 15.0 - 35.0 µm/m-°C @Temperature 50.0 - 100 °C |
8.33 - 19.4 µin/in-°F @Temperature 122 - 212 °F |
longitudinal; ISO 11359-2 |
Raschig Group MELOPLAS® 152.7 MF Cellulose-reinforced MF molding compound in white and colored shades. High surface hardness, very good UV stability, very good resistance to chemicals also to foodstuff ingredients, physiologically.. |
|||
CTE, linear | 15.0 - 35.0 µm/m-°C @Temperature 50.0 - 100 °C |
8.33 - 19.4 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group MELOPLAS® 181 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. High surface hardness, good electrical properties, good mechanical strength, high UV and heat resistanc.. |
|||
CTE, linear | 15.0 - 35.0 µm/m-°C @Temperature 50.0 - 100 °C |
8.33 - 19.4 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group MELOPLAS® 181.5 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. Very good electrical properties, high surface hardness, good mechanical strength, high UV and heat resis.. |
|||
CTE, linear | 15.0 - 35.0 µm/m-°C @Temperature 50.0 - 100 °C |
8.33 - 19.4 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group MELOPLAS® 182 MF Wood flour-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in dark colors. Improved dimensional stability and electrical properties as compared with MP 180, high surf.. |
|||
CTE, linear | 15.0 - 35.0 µm/m-°C @Temperature 50.0 - 100 °C |
8.33 - 19.4 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group MELOPLAS® 183 MF Cellulose-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in white and colored shades. Improved dimensional stability and electrical properties as compared with MP 18.. |
|||
CTE, linear | 15.0 - 35.0 µm/m-°C @Temperature 50.0 - 100 °C |
8.33 - 19.4 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group MELOPLAS® 2500 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
CTE, linear | 15.0 - 35.0 µm/m-°C @Temperature 50.0 - 100 °C |
8.33 - 19.4 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group MELOPLAS® 3025 MF Cellulose-reinforced and inorganically filled MF molding compound in white and colored shades. High surface hardness, good UV and heat stability, very good resistance to chemicals - also to foodstu.. |
|||
CTE, linear | 25.0 - 35.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.9 - 19.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
SABIC Innovative Plastics NORYL HFM3015P PPE+PS (Asia Pacific) 30% GF/MF filled FR PPE/PS blend |
|||
CTE, linear | 25.0 - 35.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.9 - 19.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
SABIC Innovative Plastics NORYL CN1134 PPE+PS (Asia Pacific) 20% filled FR high modulus PPE/PS blend |
|||
CTE, linear | 30.0 - 35.0 µm/m-°C | 16.7 - 19.4 µin/in-°F | |
Master Bond Supreme 11AO Electrically Isolating Adhesive and Sealant Description: Master Bond Polymer System SURPEME 11AO is a two component epoxy resin system for high performance bonding and sealing formulated to cure at room temperature or more rapidly at elevated.. |
|||
CTE, linear | 30.0 - 35.0 µm/m-°C @Temperature 20.0 °C |
16.7 - 19.4 µin/in-°F @Temperature 68.0 °F |
|
Abatron AboCast/AboCure 8109-2 High melting point. Filled version.Processing: 100/10 pbw; 90 minute potlife; mix at 130-140°C (270 °F); cures in 16 h/120°C (250°F), 10 h/140°C (285°F), 8 h/160°C (320°F), 2 h/ 200°C (390°.. |
|||
CTE, linear | 15.0 - 35.0 µm/m-°C @Temperature 50.0 - 100 °C |
8.33 - 19.4 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group MELOPLAS® 180 MF Wood flour-reinforced, phenol-modified MF molding compound (MPF) in dark colors. High surface hardness, good mechanical strength and electrical properties, good heat resistance. Self-extinguishing .. |
|||
CTE, linear | 24.0 - 35.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.3 - 19.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
SABIC Innovative Plastics NORYL FM3020V PPE+PS (Asia Pacific) 30% filled FR high modulus foam grade |