SABIC Innovative Plastics NORYL FM3020V PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL FM3020V PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% filled FR high modulus foam grade
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Water Absorption | 0.080 % @Time 86400 sec |
0.080 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.025 - 0.030 cm/cm @Thickness 3.20 mm |
0.025 - 0.030 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 19.2 g/10 min @Load 5.00 kg, Temperature 300 °C |
19.2 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | SABIC - Japan Method |
| Elongation at Break | 6.0 % | 6.0 % | SABIC - Japan Method |
| Flexural Strength | 113 MPa | 16400 psi | ASTM D790 |
| Flexural Modulus | 6.37 GPa | 924 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 24.0 - 35.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.3 - 19.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C @Thickness 6.40 mm |
241 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs MG100 Mg(C2H3O2)2·4H2O Magnesium acetate tetrahydrate
- RheTech Products FT1002-00A Thermoplastic Polyolefin, Non-UV Stabilized, Natural
- SABIC Innovative Plastics Lexan® XHT3143 PC Copolymer (Asia Pacific)
- Loxim 821 02T HB Polypropylene Compound, 20% Talc Filled, Flame Retardant
- Teknor Apex Flexalloy® 3500-80 Polyvinyl Chloride Elastomer
- Trelleborg Emerson & Cuming Eccobond® 43 Heat Cure Catalyst
- 3M Scotch® 660 Red Cellophane Tape
- Panjin Zhongrun Chemerize 085G Low Viscosity CoPEEK
Copyright © lookpolymers.com All Rights Reserved