Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 150 µm/m-°C @Temperature 23.0 - 60.0 °C |
83.3 µin/in-°F @Temperature 73.4 - 140 °F |
|
Omnia Plastica PP Polypropylene The mechanical features of PP are better than those of PE H.D. It withstands attack by alkali and acids and consequently it is widely used for components in the chemical industry when a moderate str.. |
|||
CTE, linear | 150 µm/m-°C @Temperature 23.0 - 100 °C |
83.3 µin/in-°F @Temperature 73.4 - 212 °F |
|
Quadrant EPP PE 500 PE-HMW, virgin (ISO Data) This grade exhibits a good combination of stiffness, toughness, mechanical damping ability with wear- and abrasion resistance and can easily be welded. In less demanding applications with respect to.. |
|||
CTE, linear | 150 µm/m-°C @Temperature 20.0 °C |
83.3 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Petromont 1100 High Density Polyethylene Resin Petromont HDPE 1100 is a high-density polyethylene homopolymer resin produced using the UNIPOL® Process. This multi-purpose resin is intended primarily for use in most intermittent and continuous b.. |
|||
CTE, linear | 150 µm/m-°C @Temperature 20.0 °C |
83.3 µin/in-°F @Temperature 68.0 °F |
ISO 11359-2 |
Chevron Phillips Xtel® XE3200NA Polyphenylene Sulfide Alloy
(discontinued **) Xtel® XE3200NA is an un-reinforced high performance, PPS based alloy developed to provide exceptionally high ductility and impact resistance along with good thermal stability.Information provided b.. |
|||
CTE, linear | 150 µm/m-°C @Temperature 20.0 °C |
83.3 µin/in-°F @Temperature 68.0 °F |
DIN 53752 |
GEHR Plastics PE-HD Polyethylene HDPE Polyethylene has a good chemical resistance against almost all acids and bases, detergents and hot water. PE has good insulation properties and is easy to weld. The operating temperature is from -50.. |
|||
CTE, linear | 150 µm/m-°C @Temperature 0.000 - 70.0 °C |
83.3 µin/in-°F @Temperature 32.0 - 158 °F |
DIN 53752 |
Borealis RA130E-1498 Polypropylene Random Copolymer RA130E-1498 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is white colored. Applications: RA130E-1498 is recommended for the production of PP-R p.. |
|||
CTE, linear | 150 µm/m-°C @Temperature 0.000 - 70.0 °C |
83.3 µin/in-°F @Temperature 32.0 - 158 °F |
DIN 53752 |
Borealis RA130E-2491 Polypropylene Random Copolymer RA130E-2491 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is blue colored. Applications: domestic water, heating, relining, plumbing, and industr.. |
|||
CTE, linear | 150 µm/m-°C @Temperature 0.000 - 70.0 °C |
83.3 µin/in-°F @Temperature 32.0 - 158 °F |
DIN 53752 |
Borealis RA130E-6034 Polypropylene Random Copolymer RA130E-6034 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is green colored. Applications: domestic water, heating, relining, plumbing, and indust.. |
|||
CTE, linear | 150 µm/m-°C @Temperature -30.0 - 30.0 °C |
83.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E831 |
A. Schulman POLYPUR™ CB 1110 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
CTE, linear | 150 µm/m-°C @Temperature -30.0 - 30.0 °C |
83.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E831 |
A. Schulman POLYPUR™ FPU 1117 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
CTE, linear | 150 µm/m-°C @Temperature -30.0 - 30.0 °C |
83.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E831 |
A. Schulman POLYPUR™ CB 1110 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
CTE, linear | 150 µm/m-°C @Temperature -30.0 - 30.0 °C |
83.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E831 |
A. Schulman POLYPUR™ FPU 1117 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
CTE, linear | 150 µm/m-°C @Temperature -30.0 - 30.0 °C |
83.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E831 |
A. Schulman POLYPUR™ FPU 1117 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
CTE, linear | 150 µm/m-°C @Temperature 20.0 °C |
83.3 µin/in-°F @Temperature 68.0 °F |
|
Trelleborg Emerson & Cuming Stycast® 5954 Two-Component Silicone High Service Temp Encapsulant Features and Typical ApplicationsAbility to withstand high temperatures, thermal shock, and chemical exposure. These products are designed for heat generating electronic devices which operate in har.. |
|||
CTE, linear | 150 µm/m-°C @Temperature 20.0 °C |
83.3 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Neostar FN006 Elastomer Neostar FN006 elastomer is the second in Eastman’s series of tough, clear, durable copolyester ethers. Developed for use in the profile and automotive markets, it can also be used in packaging and .. |
|||
CTE, linear | 150 µm/m-°C @Temperature 20.0 °C |
83.3 µin/in-°F @Temperature 68.0 °F |
|
Cytec EN-2523 (Conap) Potting and Encapsulation Adhesive Polyurethane Potting and Encapsulating SystemsConathane® EN-2500 series polyurethane potting and encapsulating systems from Cytek have varying degrees of worklife, viscosity and hardness for many s.. |
|||
CTE, linear | 150 µm/m-°C @Temperature -20.0 - 32.0 °C |
83.3 µin/in-°F @Temperature -4.00 - 89.6 °F |
ASTM D696 |
DuPont™ Surlyn® 8660 Ionomer Resin, Sodium Surlyn® 8660 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. The amount of MAA and neu.. |
|||
CTE, linear | 150 µm/m-°C @Temperature -20.0 - 32.0 °C |
83.3 µin/in-°F @Temperature -4.00 - 89.6 °F |
ASTM D696 |
DuPont™ Surlyn® 9650 Ionomer Resin, Zinc Surlyn® 9650 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr.. |
|||
CTE, linear | 150 µm/m-°C @Temperature -20.0 - 32.0 °C |
83.3 µin/in-°F @Temperature -4.00 - 89.6 °F |
ASTM D696 |
DuPont™ Surlyn® 9950 Ionomer Resin, Zinc Surlyn® 9950 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr.. |
|||
CTE, linear | 150 µm/m-°C @Temperature 20.0 °C |
83.3 µin/in-°F @Temperature 68.0 °F |
|
Arkema Group Rilsan® Fine Powders Natural Polyamide 11 Rilsan® fine powder coatings offer weatherability, long-lasting adhesion, chalk resistance, chemical resistance to aliphatic hydrocarbons, bases, salt solutions, oils, greases and other petroleum p.. |
|||
CTE, linear | 150 µm/m-°C @Temperature 20.0 °C |
83.3 µin/in-°F @Temperature 68.0 °F |
|
Arkema Group Rilsan® Fine Powders Polyamide 11 Rilsan® fine powder coatings offer weatherability, long-lasting adhesion, chalk resistance, chemical resistance to aliphatic hydrocarbons, bases, salt solutions, oils, greases and other petroleum p.. |
|||
CTE, linear | 150 µm/m-°C @Temperature 20.0 °C |
83.3 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
CENTROPLAST CENTROLEN PP-H Polypropylene homopolymer This plastic is a low density, easily machined material that can be welded and has good chemical resistance. Applications include filter housings, chemical pump components and apparatus engineering.. |
|||
CTE, linear | 150 - 180 µm/m-°C @Temperature 20.0 °C |
83.3 - 100 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Solvay Specialty Polymers Solef® 20810 PVDF Copolymer
(discontinued **) Key features of this grade: Li Battery, Virgin. Recommended processing is solution. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crysta.. |
|||
CTE, linear | 150 µm/m-°C @Temperature -30.0 - 30.0 °C |
83.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E831 |
A. Schulman POLYPUR™ CB 1110 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
CTE, linear | 150 µm/m-°C | 83.3 µin/in-°F | |
Resinlab® UR3001HP Clear Urethane Encapsulant Resinlab™ UR3001HP Clear is a clear, two component, room temperature curing urethane encapsulating system. It is designed to cure completely at room temperature. UR3001HP Clear provides excellent e.. |