- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 199 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 199 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Nylene® PA6/6 Mineral Filled 6140 HS Nylon 6/6 40% Mineral Filler; Property data for dry as molded samples.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Polymer Resources NY6-G13-[color]H Nylon, 13% Glass Reinforced, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Polymer Resources TP-FRG30 Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant Polybutylene Terephthalate, 30% Glass Reinforced, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| PTS Trimid® N6-G15HL 15% GFR Heat Stabilized Nylon 6 with Lube Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP COLORCOMP J1000R PES (Europe-Africa-Middle East) LNP* COLORCOMP* J1000R is a compound based on Polyethersulfone resin. Added features include : Mold Release |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Resinoid 2225 Phenolic Molding, Cellulose Reinforced Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Polymer Resources NY6-G13-[color]-H Nylon 6, 13% Glass Reinforced, Heat Stabilized Nylon 6, 13% Glass Reinforced, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 - 240 °C | 390 - 464 °F | Average value: 214 °C Grade Count:3 |
| Overview of materials for Phenolic, Resole, Mineral/Flock Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Resole, Mineral/Flock Filled". Each property range of values reported is minimum and maximum v.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Lubricomp JL003 PES LNP* Lubricomp* JL003 is a compound based on Polyethersulfone resin containing PTFE.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C @Thickness 6.40 mm |
390 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem 1110R PEI Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM 2312EPR PEI (Asia Pacific) 30% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem 2312EPR PEI (Europe-Africa-Middle East) 30% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the Eu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Techmer ES Plaslube® J-4/30/TF/13/SI/2 BK223 PA6/12 |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Techmer ES Plaslube® J-4/30/TF/15 Nylon 612, 30% GFR, 15% PTFE Plaslube glass fiber reinforced polytetrafluoroethylene (PTFE) lubricated nylon 612 grades offer a unique balance of excellent wear and friction performance with good dimensional stability and mecha.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM 1000E PEI (Europe-Africa-Middle East) Transparent, standard flow Polyetherimide (Tg 217C) with internal mold release. Resin is RoHS compliant. US FDA and EU Food Contact compliant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM 1000EF PEI Transparent, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, U.S. FDA and EU Food Contact compliant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP 9X11428J PPS LNP* THERMOCOMP* 9X11428J is a compound based on Polyphenylsulfone containing Proprietary Fillers. Added features of this material include: Healthcare, Low Extractable. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP PF008QS PA 6 LNP THERMOCOMP* PF008QS is a compound based on Nylon 6 resin containing 40% Glass Fiber. Added features of this material include: Heat Stabilized, Reduced Moisture. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| PlastxWorld Veroplas PB3301F Nylon 66 flame retarded (UL94 V0), 30% glass filled injection molding gradeInformation provided by PlastxWorld Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Clariant PBTSP0008WT-199 Polybutylene Terephthalate, Glass Reinforced, Flame Retardant Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Clariant Renol BR2065 Nylon 66, Mineral/Glass Reinforced Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ISO 75 |
| BASF Ultramid® 8231G HS BK-106 14% Glass Filled PA6 (Dry) Ultramid 8231G HS BK-106 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffnes.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ISO 75 |
| BASF Ultramid® B3GM35 Q643 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid B3GM35 Q643 is a 40% combined glass-fiber and mineral reinforced injection molding PA6 grade. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 421 Polyester - PBT, Glass/Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.45% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| A. Schulman ComAlloy Comtuf® 631 Nylon 6/6, Glass Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.13% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® PBT GF15 FR X 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 15% Filler by WeightFeatures: Flame RetardantProcessing Method: Injection MoldingInformation provided by TP Composites, In.. |
|||