- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 153 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 153 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 - 195 °C | 153 - 383 °F | Average value: 142 °C Grade Count:5 |
| Overview of materials for Thermoset Polyurethane, Liquid This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Liquid". Each property range of values reported is minimum and maximum values of.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C @Thickness 3.18 mm |
153 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| PolyOne Maxxam™ FR PE 161-1A Polyethylene, High Density (HDPE) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C @Thickness 4.00 mm |
153 °F @Thickness 0.157 in |
10.0 mm wide molded rod; ISO 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® ESD 1100
(discontinued **) PRE-ELEC ESD 1100 is a static dissipative thermoplastic compound based on PETG. The dissipative property is permanent and built into the polymer chain. PRE-ELEC ESD 1100 has been developed for the e.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | 120°C/h; ASTM D648 |
| Total Finaclear® 530 Clear Impact Polystyrene
(discontinued **) Finaclear® 530 is a clear high styrenic styrene-butadiene (SBS) elastomer, providing dramatically improved impact properties and tear resistance to finished articles, when used in blends with other.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Chevron Phillips HiD® 9404 HDPE Blow Molding Resin
(discontinued **) Resin Type: linear copolymerCharacteristics: medium molecular weight distributions, wide range of processing conditions, low parison sag, good stress crack resistance. Federal specification LP390C .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| ExxonMobil HD 6605.29 Injection Molding Resin
(discontinued **) HD 6605 is a narrow molecular weight hexene copolymer designed for a wide range of injection molding applications, offering excellent ESCR with good stiffness-toughness balance. Ideally suited for .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| ExxonMobil HD 6714.17 Injection Molding Resin
(discontinued **) HD 6714 is a narrow molecular weight hexene copolymer designed for outstanding processability to maximize injection molding productivity. This resin is ideally suited for thin wall multicavity part.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| ExxonMobil HD 6761.17 Injection Molding Resin
(discontinued **) HD 6761 is a narrow molecular weight hexene copolymer designed for good processability and excellent balance of ESCR, Toughness, and Stiffness properties. This resin is ideally suited for a heavy-d.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Braskem ES 002G HDPE Pipe Extrusion Polyethylene
(discontinued **) Applications: Flat and corrugated pipes extrusion for mining, energy and telecommunication systems; piping in sewage systems. Information provided by Braskem |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Flint Hills P6E5A-004 Impact Copolymer Polypropylene Impact copolymer, UL certified.Features: LTHA, controlled rheology, and extra high impact strength.Applications: Injection molding: automotive, toys, and containers.Former Huntsman polypropylene pro.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Ineos K44-11-128 HDPE Ineos K44-11-128 is a high molecular weight, high density polyethylene copolymer intended for large part blow molding where the finished product demands good physical performance and low color. Thi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 7001 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin DescriptionSuperlinear XL 0360 is compounded rotational molding resin based on metallocean catalyst technology. This technology allows for high impact and excellent stiffness. It is typically used.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin DescriptionSuperlinear XL 0360 is compounded rotational molding resin based on metallocean catalyst technology. This technology allows for high impact and excellent stiffness. It is typically used.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 7001 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin DescriptionSuperlinear XL 0360 is compounded rotational molding resin based on metallocean catalyst technology. This technology allows for high impact and excellent stiffness. It is typically used.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 7001 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin DescriptionSuperlinear XL 0360 is compounded rotational molding resin based on metallocean catalyst technology. This technology allows for high impact and excellent stiffness. It is typically used.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin DescriptionSuperlinear XL 0360 is compounded rotational molding resin based on metallocean catalyst technology. This technology allows for high impact and excellent stiffness. It is typically used.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Eastman PROVISTA Copolymer PETG Copolyester Color, b* CIELAB, Illuminant D6500, 10° Observer is 0.61 per ASTM D 2244.Product Description: PROVISTA Copolymer is a resin specifically developed for extrusion into profiles where aesthetics like.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | |
| Covestro Baydur® GS PUR Polyurethane Polyurethane casting system for the production of solid components. Pressureless casting into open or closed molds, fast demold times, good rot resistance. Combines easily with other materials.Infor.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| ExxonMobil HD 6719.17 Injection Molding Resin Product Description: HD 6719 is a narrow molecular weight hexane copolymer designed for a wide rage of injection molding applications, combining easy processability with good toughness properties. I.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.2 °C | 153 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Dow UNIVAL™ DMDA-6220 NT 7 High Density Polyethylene Resin (HDPE) Moderate swell Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a UNIVAL™ DMDA-6220 NT 7 is a multipurpose polymer designed for high speed production of blow molded containers used to package househol.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.2 °C | 153 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Dow UNIVAL™ DMDC-6143 NT 7 High Density Polyethylene Resin (HDPE) Excellent parison melt strength / low sag Good extrudability / process-ability Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a UNIVAL™ DMDC-6143 NT 7 is a polymer with broad molecular weight distri.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| ExxonMobil HD 6605.70 Injection Molding Resin Product Description: HD 6605.70 is a narrow molecular weight hexane copolymer designed for a wide range of injection molding applications, offering excellent ESCR with good stiffness-toughness balan.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| ExxonMobil HD 6733.17 Injection Molding Resin Product Description: HD 6733 is a narrow molecular weight hexane copolymer designed to maximize injection molding speed and productivity in thing wall articles. Lower processing temperatures enable .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| ExxonMobil HD 8660.29 Rotational Molding Resin Product Description: HD 8660 series are high density hexane copolymers designed to offer superior toughness and stiffness. They are ideally suited for applications that require the optimum balance o.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
| ExxonMobil HDP8660.29 Rotational Molding Resin Product Description: HD 8660 series are high density hexane copolymers designed to offer superior toughness and stiffness. They are ideally suited for applications that require the optimum balance o.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | |
| Addcomp PRIEX® Ionomer 33101 HDPE Ionomers will be used toStrengthen rigidity and hardness while maintaining impact resistance in polyolefinsMaintain adhesion even under contaminated conditions especially in fatty substratesReduce t.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | |
| Addcomp PRIEX® Ionomer 30101 HDPE Ionomers will be used toStrengthen rigidity and hardness while maintaining impact resistance in polyolefinsMaintain adhesion even under contaminated conditions especially in fatty substratesReduce t.. |
|||