ExxonMobil HD 6605.29 Injection Molding Resin (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil HD 6605.29 Injection Molding Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

HD 6605 is a narrow molecular weight hexene copolymer designed for a wide range of injection molding applications, offering excellent ESCR with good stiffness-toughness balance. Ideally suited for articles requiring rugged physical performance in cold temperature environments.Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.948 g/cc	0.0342 lb/in³	ASTM D4883
Environmental Stress Crack Resistance	18 hour	18 hour	Cond. B, 10%; ASTM D1693
Melt Flow	5.0 g/10 min @Load 2.16 kg, Temperature 190 °C	5.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	23.2 MPa	3360 psi	ASTM D638
Elongation at Break	48 %	48 %	ASTM D638
Flexural Modulus	0.7060 GPa	102.4 ksi	1% Secant; ASTM D790
Izod Impact, Notched	0.705 J/cm @Temperature -40.0 °C	1.32 ft-lb/in @Temperature -40.0 °F	ASTM D256
Tensile Impact Strength	326 kJ/m² @Temperature -40.0 °C	155 ft-lb/in² @Temperature -40.0 °F	ASTM D1822

Thermal Properties	Metric	English	Comments
Melting Point	130 °C	266 °F	ASTM D3418
Crystallization Temperature	114 °C	237 °F	ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi)	67.0 °C	153 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	38.0 °C	100 °F	ASTM D648
Brittleness Temperature	<= -70.0 °C	<= -94.0 °F	ASTM D746

Descriptive Properties	Value	Comments
Features	UV-8 Protection Package
Form	Pellet