Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 - 195 °C | 153 - 383 °F | Average value: 142 °C Grade Count:5 |
Overview of materials for Thermoset Polyurethane, Liquid This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Liquid". Each property range of values reported is minimum and maximum values of.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C @Thickness 3.18 mm |
153 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
PolyOne Maxxam™ FR PE 161-1A Polyethylene, High Density (HDPE) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C @Thickness 4.00 mm |
153 °F @Thickness 0.157 in |
10.0 mm wide molded rod; ISO 75/Method Bf |
Premix Thermoplastics PRE-ELEC® ESD 1100
(discontinued **) PRE-ELEC ESD 1100 is a static dissipative thermoplastic compound based on PETG. The dissipative property is permanent and built into the polymer chain. PRE-ELEC ESD 1100 has been developed for the e.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | 120°C/h; ASTM D648 |
Total Finaclear® 530 Clear Impact Polystyrene
(discontinued **) Finaclear® 530 is a clear high styrenic styrene-butadiene (SBS) elastomer, providing dramatically improved impact properties and tear resistance to finished articles, when used in blends with other.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
ExxonMobil HD 6761.17 Injection Molding Resin
(discontinued **) HD 6761 is a narrow molecular weight hexene copolymer designed for good processability and excellent balance of ESCR, Toughness, and Stiffness properties. This resin is ideally suited for a heavy-d.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C @Thickness 3.18 mm |
153 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
PolyOne Maxxam™ FR PE 161 HDPE
(discontinued **) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
Braskem BS 002J HDPE Blow Molding Polyethylene
(discontinued **) Applications: Bottles up to 60 liters with high ESCR; bottles for surface-active agents. Information provided by Braskem |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
Braskem ES 002G HDPE Pipe Extrusion Polyethylene
(discontinued **) Applications: Flat and corrugated pipes extrusion for mining, energy and telecommunication systems; piping in sewage systems. Information provided by Braskem |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
Flint Hills P6E5A-004 Impact Copolymer Polypropylene Impact copolymer, UL certified.Features: LTHA, controlled rheology, and extra high impact strength.Applications: Injection molding: automotive, toys, and containers.Former Huntsman polypropylene pro.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ISO 75 |
MRC Polymers MAXTEL™ 620-BK Polypropylene Copolymer • For injection molding• Excellent process ability with high flow and high impact.Information provided by MRC Polymers Inc. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
Ineos K44-11-128 HDPE Ineos K44-11-128 is a high molecular weight, high density polyethylene copolymer intended for large part blow molding where the finished product demands good physical performance and low color. Thi.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM Test |
Styrolution Styrolux 3G55 SBC Styrolux 3G55 is a thermoplastic styrene-butadiene block copolymer which is suitable for film and sheet extrusion, and thermoforming. It offers and outstanding combination of crystal clarity and ex.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 7001 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 7001 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin DescriptionSuperlinear XL 0360 is compounded rotational molding resin based on metallocean catalyst technology. This technology allows for high impact and excellent stiffness. It is typically used.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 7001 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 7001 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin DescriptionSuperlinear XL 0360 is compounded rotational molding resin based on metallocean catalyst technology. This technology allows for high impact and excellent stiffness. It is typically used.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 7001 Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin DescriptionSuperlinear XL 0360 is compounded rotational molding resin based on metallocean catalyst technology. This technology allows for high impact and excellent stiffness. It is typically used.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | Absolute Drying; ASTM-D648 |
Toyobo GLAMIDE® T-222SA Nylon/Elastomer GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin DescriptionSuperlinear XL 0360 is compounded rotational molding resin based on metallocean catalyst technology. This technology allows for high impact and excellent stiffness. It is typically used.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
Eastman Provista MP001 Copolymer Provista Copolymer MP001 is a resin specifically developed for extrusion into profiles where aesthetics such as high clarity and gloss, coupled with design flexibility, drive demand. Compared to com.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
Eastman Provista UVI Copolymer Provista UVI is a Provista copolymer with an indoor/outdoor UV package added to prevent yellowing caused by light. Provista copolymer is a resin specifically developed for extrusion into profiles wh.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | |
Covestro Baydur® GS PUR Polyurethane Polyurethane casting system for the production of solid components. Pressureless casting into open or closed molds, fast demold times, good rot resistance. Combines easily with other materials.Infor.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
ExxonMobil HD 6719.17 Injection Molding Resin Product Description: HD 6719 is a narrow molecular weight hexane copolymer designed for a wide rage of injection molding applications, combining easy processability with good toughness properties. I.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
ExxonMobil HD 6733.17 Injection Molding Resin Product Description: HD 6733 is a narrow molecular weight hexane copolymer designed to maximize injection molding speed and productivity in thing wall articles. Lower processing temperatures enable .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 |
ExxonMobil HD 8660.29 Rotational Molding Resin Product Description: HD 8660 series are high density hexane copolymers designed to offer superior toughness and stiffness. They are ideally suited for applications that require the optimum balance o.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM-D648 |
Braskem Prisma 2910 RACO Random Polypropylene Copolymer Prisma 2910 is a high melt flow rate random copolymer designed for injection molding applications. This product offers high impact strength at low temperatures and excellent processability. Its appl.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | |
Addcomp PRIEX® Ionomer 30101 HDPE Ionomers will be used toStrengthen rigidity and hardness while maintaining impact resistance in polyolefinsMaintain adhesion even under contaminated conditions especially in fatty substratesReduce t.. |