Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 16.5 - 17.5 µm/m-°C @Temperature 20.0 - 300 °C |
9.17 - 9.72 µin/in-°F @Temperature 68.0 - 572 °F |
|
PEAK Werkstoff DISPAL S225 Aluminum Alloy, AlSi35Fe2Ni, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 21.1 - 816 °C |
9.17 µin/in-°F @Temperature 70.0 - 1500 °F |
|
Kennametal Stellite Stellite® 31 PM with P/M Processing; heat treated at 93°C (200°F) and water quenched Typical applications include, miscellaneous wear parts. Data provided by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 200 °C |
9.17 µin/in-°F @Temperature 68.0 - 392 °F |
|
Industeel CLC 17.13.5 LN Modified 317LN Mo 4% Austenitic Stainless Steel Description: CLC 17-13-5LN (317LNM) is a Nitrogen alloyed austenitic stainless steel with a high Molybdenum addition (=4%). Alloy CLC 17-13-5LN (317LNM) exhibits austenitic microstructure free of de.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 200 °C |
9.17 µin/in-°F @Temperature 68.0 - 392 °F |
|
Industeel CLC 18.10 Nb Niobium Stabilized 18Cr-10Ni Austenitic Stainless Steel CLC 18-10Nb is a 18Cr-10Ni austenitic stainless steel stabilized with specific Nb addition. This kind of steel is one of the basic grades of the stainless steels range. Niobium bearing and its low c.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 300 °C |
9.17 µin/in-°F @Temperature 68.0 - 572 °F |
|
Industeel URANUS® B26 6 Mo High Performance Super-Austenitic Stainless Steel with PREN = 43 Description: URANUS® B26 (UR B26) is a 25% Ni, 20% Cr, 6% Mo superaustenitic stainless steel grade with 0.2 % nitrogen additions, particularly designed for high structural stability and high corr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, vacuum investment castings, solution treated Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 200 °C |
9.17 µin/in-°F @Temperature 68.0 - 392 °F |
|
Schmolz + Bickenbach UGIMA® 304 Cu Stainless Steel Bar Description: 304Cu UGIMA® is an enhanced machining grade produced only by Ugitech, providing the ultimate level of machinability available in an non-resulfurized austenitic stainless steel. 304Cu.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 100 °C |
9.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
ATI Allegheny Ludlum Type 317 Stainless Steel, UNS S31700 This is a molybdenum-bearing austenitic stainless steels which is more resistant to general corrosion and pitting/crevice corrosion than the conventional chromium-nickel austenitic stainless steels .. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 300 °C |
9.17 µin/in-°F @Temperature 68.0 - 572 °F |
|
Industeel UREA 25.22.2 Plants Description: CLI UREA 25.22.2 chemical composition has been optimized for specific uses in Urea plants. It is a 310L modified austenitic stainless steel with low carbon, low silicon and high nitroge.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 300 °C |
9.17 µin/in-°F @Temperature 68.0 - 572 °F |
|
Industeel UREA 316L Modified 316L Mod Low Si, High Mo Stainless Steel for Urea Plants Description: UREA 316L Modified grade has been specially developed for Urea plant applications. It is a 316L modified stainless steel with extra-low silicon content and substantial higher molybdenum.. |