Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 316°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 760°C (1400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, all-weld metal, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, all-weld metal, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, all-weld metal, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 26.0 - 760 °C |
8.83 µin/in-°F @Temperature 78.8 - 1400 °F |
|
Haynes Ultimet® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 25.0 - 900 °C |
8.83 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 282® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 260 °C |
8.83 µin/in-°F @Temperature 500 °F |
|
Special Metals INCOLOY® alloy 028 Austenitic Stainless Steel INCOLOY® alloy 028 (UNS N08028/W. Nr. 1.4563) is a highly alloyed austenitic stainless steel offering resistance to a variety of corrosive media. By virtue of its contents of chromium and molybd.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 400 °C |
8.83 µin/in-°F @Temperature 752 °F |
|
Special Metals INCOLOY® alloy 864 INCOLOY® alloy 8684 (UNS S35135) was specifically developed for automotive exhaust system flexible couplings, EGR tubes, manifolds and tailpipes. It exhibits excellent fatigue resistance, therma.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 20.0 - 100 °C |
8.83 µin/in-°F @Temperature 68.0 - 212 °F |
|
ATI Allegheny Ludlum 310 Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 20.0 - 100 °C |
8.83 µin/in-°F @Temperature 68.0 - 212 °F |
|
ATI Allegheny Ludlum 310H Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 20.0 - 100 °C |
8.83 µin/in-°F @Temperature 68.0 - 212 °F |
|
ATI Allegheny Ludlum 310S Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
CTE, linear | 15.9 µm/m-°C @Temperature 20.0 - 100 °C |
8.83 µin/in-°F @Temperature 68.0 - 212 °F |
|
ATI Allegheny Ludlum 310Si Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |