- HOME
- POLYMER SEARCH
- Polymer Property : CTE, linear = 8.78 µin/in-°F
Polymer Property : CTE, linear = 8.78 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.8 µm/m-°C @Temperature 0.000 - 700 °C |
8.78 µin/in-°F @Temperature 32.0 - 1290 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 20.0 - 100 °C |
8.78 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Industeel URANUS® B26 6 Mo High Performance Super-Austenitic Stainless Steel with PREN = 43 Description: URANUS® B26 (UR B26) is a 25% Ni, 20% Cr, 6% Mo superaustenitic stainless steel grade with 0.2 % nitrogen additions, particularly designed for high structural stability and high corr.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 20.0 - 200 °C |
8.78 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Industeel URANUS® B28 High Nickel Super-Austenitic Stainless Steel Description: URANUS® B28 (UR B28) is a super-austenitic stainless steel with very high nickel (31%) and chromium (27%) contents. The molybdenum content is about 3.5%. The alloy is designed for sp.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 188 alloy, hot rolled and 1175°C solution annealed plate Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 214® alloy, 0% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 214® alloy, 10% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 214® alloy, 20% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 214® alloy, 30% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 214® alloy, 40% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 214® alloy, 40% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 214® alloy, 50% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 214® alloy, sheet, 100 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 214® alloy, sheet, 32 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 800 °C |
8.78 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 25 alloy, hot rolled and 1230°C solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 400 °C |
8.78 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes HR-120® alloy, solution heat-treated Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 214® alloy, 30% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 800 °C |
8.78 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 25 alloy, room temperature sheet after 500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 24.0 - 871 °C |
8.78 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-22® alloy, 40% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 24.0 - 871 °C |
8.78 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-22® alloy, transverse, GMAW spray weldment, 23.4 mm thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 800 °C |
8.78 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 25 alloy, room temperature after 0% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 800 °C |
8.78 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 24.0 - 871 °C |
8.78 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-22® alloy, all-weld metal, SMAW HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 24.0 - 871 °C |
8.78 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, as welded, unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 800 °C |
8.78 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 24.0 - 871 °C |
8.78 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 24.0 - 871 °C |
8.78 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
Copyright © lookpolymers.com All Rights Reserved