- Polymer Property : CTE, linear = 7.78 µin/in-°F
Polymer Property : CTE, linear = 7.78 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.0 µm/m-°C @Temperature -50.0 - 50.0 °C |
7.78 µin/in-°F @Temperature -58.0 - 122 °F |
Axial; ASTM E831 |
| Solvay Specialty Polymers Ryton® BR111BL Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® BR111BL is a glass and mineral filled polyphenylene sulfide compounds developed to provide a good combination of mechanical strength and electrical proper.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 20.0 - 300 °C |
7.78 µin/in-°F @Temperature 68.0 - 572 °F |
|
| Industeel URANUS® 35N 23.04 Duplex Stainless Steel with PREN = 24 Description: URANUS® 35N (UR 35N) is a 23% Cr, 4% Nickel, Mo free duplex stainless steel (23.04). The alloy UR 35N has similar corrosion resistance properties similar to 316L. Furthermore, its me.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 500 °C |
7.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 500 °C |
7.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 500 °C |
7.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 21.0 - 649 °C |
7.78 µin/in-°F @Temperature 69.8 - 1200 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 315 °C |
7.78 µin/in-°F @Temperature 77.0 - 599 °F |
|
| Haynes HR-160® alloy plate, aged 1000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 315 °C |
7.78 µin/in-°F @Temperature 77.0 - 599 °F |
|
| Haynes HR-160® alloy, plate, aged 8000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 315 °C |
7.78 µin/in-°F @Temperature 77.0 - 599 °F |
|
| Haynes HR-160® alloy, plate, aged 8000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 21.0 - 649 °C |
7.78 µin/in-°F @Temperature 69.8 - 1200 °F |
|
| Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 26.0 - 316 °C |
7.78 µin/in-°F @Temperature 78.8 - 601 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 26.0 - 316 °C |
7.78 µin/in-°F @Temperature 78.8 - 601 °F |
|
| Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 26.0 - 316 °C |
7.78 µin/in-°F @Temperature 78.8 - 601 °F |
|
| Haynes Ultimet® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 20.0 - 200 °C |
7.78 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Industeel URANUS® 47N+ 25 Cr Super Duplex Stainless Steel with PREN = 40 Description: CLI - SAF 2507® is a 25.07 super duplex stainless steel with 25% Cr and a PREN value higher than 40. The minimum guaranteed yield strength is 550 MPa which allows the designer to red.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 500 °C |
7.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 230® alloy, plate, 8000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 800 °C |
7.78 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 21.0 - 300 °C |
7.78 µin/in-°F @Temperature 69.8 - 572 °F |
Mean; aged |
| Special Metals DURANICKEL® 301 (UNS N03301) Cold-Drawn Rod and Bar Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Cold-Drawn Rod and Bar specifically. Other property values are typical of annealed DURANICKEL®.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 20.0 - 540 °C |
7.78 µin/in-°F @Temperature 68.0 - 1000 °F |
|
| Crucible Steel AIRKOOL® (AISI A2) Tool Steel Airkool (AISI A2) is an air-hardening medium alloy tool steel which is heat treatable to HRC 60-62. It has wear resistance intermediate between the oil hardening tool steels (O1) and the high carbon.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 500 °C |
7.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 732°C (1350°F)/8hr/AC to 621°C (1150°F)/8hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 20.0 - 1093 °C |
7.78 µin/in-°F @Temperature 68.0 - 1999 °F |
|
| ATI Allegheny Ludlum AL 453™ Stainless Steel Single phase iron-chromium ferritic stainless steel alloy. Should be annealed between 1450 and 1600°F and quickly cooled. Information provided by Allegheny Ludlum |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 500 °C |
7.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 21.0 - 649 °C |
7.78 µin/in-°F @Temperature 69.8 - 1200 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 30.0 - 400 °C |
7.78 µin/in-°F @Temperature 86.0 - 752 °F |
|
| Ametek Molybdenum-Copper Composite AMC 3169 Information supplied by Ametek Specialty Metal Products.The material is available as finished parts with the following maximum dimensions:Width: 6 inches (152 mm)Thickness: 0.150 inches (3.8 mm)Leng.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 500 °C |
7.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 230® alloy plate, 16000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 21.0 - 649 °C |
7.78 µin/in-°F @Temperature 69.8 - 1200 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||