- Polymer Property : CTE, linear = 7.28 µin/in-°F
Polymer Property : CTE, linear = 7.28 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.1 µm/m-°C @Temperature 0.000 - 600 °C |
7.28 µin/in-°F @Temperature 32.0 - 1110 °F |
|
| Kennametal Stellite Stellite® 3 PM with P/M Processing Typical applications include (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) diesel engine exhaust, fluid valve seats, saw cutt.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 200 °C |
7.28 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Industeel CREUSABRO® 4800 Advanced Technology in Wear Steel Description: CREUSABRO® 4800(P) is a wear resistant steel offering up to 50% extra in service life compared with a 400 HB water quenched steel. CREUSABRO® 4800(P) combines several modern metal.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 427 °C |
7.28 µin/in-°F @Temperature 68.0 - 801 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 427 °C |
7.28 µin/in-°F @Temperature 68.0 - 801 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 427 °C |
7.28 µin/in-°F @Temperature 68.0 - 801 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 427 °C |
7.28 µin/in-°F @Temperature 68.0 - 801 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 427 °C |
7.28 µin/in-°F @Temperature 68.0 - 801 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 427 °C |
7.28 µin/in-°F @Temperature 68.0 - 801 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.28 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 282® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 800 °C |
7.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes Hastelloy® B-3® alloy, 20% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 500 °C |
7.28 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Plate, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 21.0 - 648 °C |
7.28 µin/in-°F @Temperature 69.8 - 1200 °F |
|
| Latrobe Dynaflex® VAC-ARC High Strength Alloy Steel DYNAFLEX VAC-ARC steel is a medium alloyed, air hardening ultra high strength grade designed for structural applications requiring room temperature tensile strengths of 220,000 to 300,000 psi. Due .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 300 °C |
7.28 µin/in-°F @Temperature 68.0 - 572 °F |
|
| Schott BG39 Band Pass Filter Ionically colored glass. Data provided by the manufacturer, Schott Glas Mainz. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 599 °C |
7.28 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| Bohler-Uddeholm BÖHLER K340 ISODUR® Premium Cold Work Steel BÖHLER K340 ISODUR is a universal cold work tool steel with which you‘ll be making money and just when blanking coins, but also when: blanking, cutting, cold rolling, extruding, deep drawing and b.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 699 °C |
7.28 µin/in-°F @Temperature 68.0 - 1290 °F |
|
| Bohler-Uddeholm BÖHLER K340 ISODUR® Premium Cold Work Steel BÖHLER K340 ISODUR is a universal cold work tool steel with which you‘ll be making money and just when blanking coins, but also when: blanking, cutting, cold rolling, extruding, deep drawing and b.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 23.0 - 982 °C |
7.28 µin/in-°F @Temperature 73.4 - 1800 °F |
|
| Carpenter Chrome Core® 18-FM Solenoid Quality Stainless Steel, Annealed Data provided by Carpenter Technology Corporation.This is a soft ferritic material designed for operation in more corrosive environments than tolerated by 18% Cr-Fe Type 430 stainless. This new mat.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, 50% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 500 °C |
7.28 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 427 °C |
7.28 µin/in-°F @Temperature 68.0 - 801 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||