Polymer Property : CTE, linear = 6.83 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.3 µm/m-°C @Temperature 0.000 - 400 °C |
6.83 µin/in-°F @Temperature 32.0 - 752 °F |
|
| Kennametal Stellite Stellite® STAR cast Applications: Vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, wear pads, pins, balls, hardfa.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 0.000 - 400 °C |
6.83 µin/in-°F @Temperature 32.0 - 752 °F |
|
| Kennametal Stellite Stellite® STAR with P/M Processing Applications: Vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, wear pads, pins, balls, hardfa.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 600 °C |
6.83 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed, 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595°C (1100°F) for 2 hours Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, hot rolled and 1230°C solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 21.0 - 100 °C |
6.83 µin/in-°F @Temperature 69.8 - 212 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2025°F (1107°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 600 °C |
6.83 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 600 °C |
6.83 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 242® alloy, after 1000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 600 °C |
6.83 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 600 °C |
6.83 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed, 40% cold work, aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, room temperature sheet after 1000 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, room temperature sheet after 500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 21.0 - 100 °C |
6.83 µin/in-°F @Temperature 69.8 - 212 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 20.0 - 200 °C |
6.83 µin/in-°F @Temperature 68.0 - 392 °F |
Hardened and tempered to 56 HRC |
| Assab Steels CARMO Cold Work Steel CARMO is a high-strength, flame-induction and through hardening steel delivered prehardened to 240-270 HB.The surface of the steel can be flame-hardened without water cooling to a hardness of 58±2.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 20.0 - 400 °C |
6.83 µin/in-°F @Temperature 68.0 - 752 °F |
|
| Bohler-Uddeholm BÖHLER W360 ISOBLOC® Hot Work Tool Steel BÖHLER W360 ISOBLOC was developed as a tool steel for dies and punches in warm and hot forging. The steel can be used for a variety of applications where hardness and toughness are required. Prope.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 21.0 - 100 °C |
6.83 µin/in-°F @Temperature 69.8 - 212 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 21.0 - 316 °C |
6.83 µin/in-°F @Temperature 69.8 - 601 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 21.0 - 316 °C |
6.83 µin/in-°F @Temperature 69.8 - 601 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 21.0 - 316 °C |
6.83 µin/in-°F @Temperature 69.8 - 601 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 20.0 - 400 °C |
6.83 µin/in-°F @Temperature 68.0 - 752 °F |
|
| Schmolz + Bickenbach Cryodur® 2990 Cold Work Die Steel Description: Newly developed ledeburitic cold-work steel with high hardness, good toughness and high tempering resistance combined with high wear resistance.Applications: Cutting and punching tools .. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 25.0 - 100 °C |
6.83 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 12.3 µm/m-°C @Temperature 21.0 - 316 °C |
6.83 µin/in-°F @Temperature 69.8 - 601 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||