Kennametal Stellite Stellite® STAR cast

Category Metal , Nonferrous Metal , Cobalt Alloy , Superalloy
Manufacturer Kennametal Stellite
Trade Name Stellite®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kennametal Stellite Stellite® STAR cast.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: Vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, wear pads, pins, balls, hardfaces when crack free deposits are not required.Corrosion: Corrosion resistance similar to Stellite alloy 3, but inferior to Stellite alloy 6. Excellent oxidation resistance at low temperatures, but not recommended for reducing environments. Corrosion will vary depending on concentration, temperature, stress, and type of contaminants so exposure tests are recommended.Machinability: Stress relieve before and during machining by holding at 900°C (1650°F) for four hours and slow cool.Wear: High tungsten content results in excellent hot hardness and low stress abrasion resistance superior to Stellite alloy 3. Wear resistance is similar to Stellite alloy 3 and is non-galling when mated with other Stellite alloys.Data provided by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc.
Physical Properties Metric English Comments
Density 8.58 g/cc
0.310 lb/in³
P/M (98%)
8.76 g/cc
0.316 lb/in³
Theoretical
Mechanical Properties Metric English Comments
Hardness, Rockwell C 56
56
Hot hardness.
Tensile Strength, Ultimate 428 MPa
62100 psi
Elongation at Break <= 1.0 %
<= 1.0 %
in 25.4 mm
Modulus of Elasticity 258 GPa
37400 ksi
Thermal Properties Metric English Comments
CTE, linear 12.0 µm/m-°C

@Temperature 0.000 - 100 °C
 6.67 µin/in-°F

@Temperature 32.0 - 212 °F
12.1 µm/m-°C

@Temperature 0.000 - 200 °C
 6.72 µin/in-°F

@Temperature 32.0 - 392 °F
12.2 µm/m-°C

@Temperature 0.000 - 300 °C
 6.78 µin/in-°F

@Temperature 32.0 - 572 °F
12.3 µm/m-°C

@Temperature 0.000 - 400 °C
 6.83 µin/in-°F

@Temperature 32.0 - 752 °F
12.6 µm/m-°C

@Temperature 0.000 - 500 °C
 7.00 µin/in-°F

@Temperature 32.0 - 932 °F
12.8 µm/m-°C

@Temperature 0.000 - 600 °C
 7.11 µin/in-°F

@Temperature 32.0 - 1110 °F
13.2 µm/m-°C

@Temperature 0.000 - 700 °C
 7.33 µin/in-°F

@Temperature 32.0 - 1290 °F
13.6 µm/m-°C

@Temperature 0.000 - 800 °C
 7.56 µin/in-°F

@Temperature 32.0 - 1470 °F
14.3 µm/m-°C

@Temperature 0.000 - 900 °C
 7.94 µin/in-°F

@Temperature 32.0 - 1650 °F
15.1 µm/m-°C

@Temperature 0.000 - 1000 °C
 8.39 µin/in-°F

@Temperature 32.0 - 1830 °F
Melting Point 1215 - 1299 °C
2219 - 2370 °F
Solidus 1215 °C
2219 °F
Liquidus 1300 °C
2370 °F
Component Elements Properties Metric English Comments
Boron, B <= 1.0 %
<= 1.0 %
Carbon, C 2.5 %
2.5 %
Chromium, Cr 32.5 %
32.5 %
Cobalt, Co 36.5 %
36.5 %
As remainder
Iron, Fe <= 3.0 %
<= 3.0 %
Manganese, Mn <= 1.0 %
<= 1.0 %
Nickel, Ni <= 3.0 %
<= 3.0 %
Other <= 2.0 %
<= 2.0 %
Silicon, Si <= 1.0 %
<= 1.0 %
Tungsten, W 17.5 %
17.5 %
Electrical Properties Metric English Comments
Magnetic Permeability <= 1.20

@Temperature 22.0 °C
 <= 1.20

@Temperature 71.6 °F
 200 Oersted