- Polymer Property : CTE, linear = 16.6 µm/m-°C
Polymer Property : CTE, linear = 16.6 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.6 µm/m-°C @Temperature 21.1 - 871 °C |
9.22 µin/in-°F @Temperature 70.0 - 1600 °F |
|
| Kennametal Stellite Stellite® 31 PM cast Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we.. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 25.0 - 800 °C |
9.22 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 214® alloy sheet Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 25.0 - 800 °C |
9.22 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 214® alloy, 20% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 25.0 - 800 °C |
9.22 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 214® alloy, 40% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 25.0 - 800 °C |
9.22 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 25.0 - 800 °C |
9.22 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 214® alloy, sheet, 100 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 25.0 - 800 °C |
9.22 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 214® alloy, sheet, 1000 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 25.0 - 800 °C |
9.22 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 214® alloy, sheet, 32 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 20.0 - 1000 °C |
9.22 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| Haynes Hastelloy® X alloy, sheet Solid-solution-strengthened with very good high-temperature strength and very good resistance to oxidizing environments up to about 1095°C, and good carburization resistance. Applications includ.. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 25.0 - 800 °C |
9.22 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes HR-160® alloy, plate, aged 1000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 25.0 - 800 °C |
9.22 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes HR-160® alloy, plate, aged 4000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 25.0 - 800 °C |
9.22 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 214® alloy, 30% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 21.0 - 900 °C |
9.22 µin/in-°F @Temperature 69.8 - 1650 °F |
Mean |
| Special Metals DURANICKEL® 301 (UNS N03301) Annealed and Aged Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Annealed and Aged Strip specifically. Other property values are typical of aged DURANICKEL® alloy 301 or.. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 21.0 - 900 °C |
9.22 µin/in-°F @Temperature 69.8 - 1650 °F |
Mean; aged |
| Special Metals DURANICKEL® 301 (UNS N03301) Half-Hard Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Half-Hard Strip specifically. Other property values are typical of annealed DURANICKEL® alloy 301 or the.. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 21.0 - 900 °C |
9.22 µin/in-°F @Temperature 69.8 - 1650 °F |
Mean |
| Special Metals DURANICKEL® 301 (UNS N03301) Hot-Finished and Aged Rod and Bar Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Hot-Finished and Aged Rod and Bar specifically. Other property values are typical of aged DURANIC.. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 20.0 - 799 °C |
9.20 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Carlson 904L Austenitic Stainless Steel General Description904L is an austenitic nickel-chromium stainless steel with molybdenum and copper additions. The elevated nickel and chromium content of 904L make it resistant to corrosion in a w.. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 0.000 - 100 °C |
9.22 µin/in-°F @Temperature 32.0 - 212 °F |
|
| AK Steel 321 Austenitic Stainless steel AK Steel 321 is a stabilized austenitic stainless steel similar to Type 304 but with a titanium addition. This titanium addition reduces or prevents carbide precipitation during welding and in 427 .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 26.0 - 982 °C |
9.22 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| ATI Allegheny Ludlum Altemp® HX Nickel-Based superalloy Characteristics: outstanding resistance to oxidation at high temperatures, exceptional strength at elevated temperatures, good fabricability, good machinability in annealed condition, work hardening.. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 20.0 - 100 °C |
9.22 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 302, 40% Cold Rolled (UNS S30200) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 20.0 - 100 °C |
9.22 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304, 10% Cold Rolled (UNS S30400) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 20.0 - 100 °C |
9.22 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304, 50% Cold Rolled (UNS S30400) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 20.0 - 100 °C |
9.22 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304L, 0% Cold Rolled (UNS S30403) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 20.0 - 100 °C |
9.22 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304L, 60% Cold Rolled (UNS S30403) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 20.0 - 100 °C |
9.22 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum Stainless Steel Free Machining Grade Type 303, Annealed (UNS S30300) Allegheny Ludlum's 303 is a free-machining stainless steel specifically designed to exhibit improved machinability. These modifications retain, in so far as possible, the good mechanical properties.. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 20.0 - 100 °C |
9.22 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum Stainless Steel Type 201L, 50% Cold Work (UNS S20103) Allegheny Ludlum Types 201 and 201L have the greatest tonnage of the Cr-Ni-Mn steels (200 series). Type 201L provides advantages over the 18-8 grades in certain applications. Lower cost manganese .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 20.0 - 100 °C |
9.22 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum Stainless Steel Type 201L, 60% Cold Work (UNS S20103) Allegheny Ludlum Types 201 and 201L have the greatest tonnage of the Cr-Ni-Mn steels (200 series). Type 201L provides advantages over the 18-8 grades in certain applications. Lower cost manganese .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 20.0 - 100 °C |
9.22 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 302, 60% Cold Rolled (UNS S30200) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 20.0 - 100 °C |
9.22 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum Stainless Steel Type 201, 30% Cold Work (UNS S20100) Allegheny Ludlum Type 201 and 201L have the greatest tonnage of the Cr-Ni-Mn steels (200 series). Type 201 provides advantages over the 18-8 grades in certain applications. Lower cost manganese an.. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 20.0 - 100 °C |
9.22 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum Stainless Steel Type 301, 1/4 Hard (UNS S30100) Allegheny Ludlum Type 301 is a high strength grade of steel available in six conditions or tempers, its resistance to atmosphere corrosion and its bright, attractive surface make it an excellent cho.. |
|||
| CTE, linear | 16.6 µm/m-°C @Temperature 20.0 - 100 °C |
9.22 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum Stainless Steel Type 301, annealed (UNS S30100) Allegheny Ludlum Type 301 is a high strength grade of steel available in six conditions or tempers, its resistance to atmosphere corrosion and its bright, attractive surface make it an excellent cho.. |
|||