- HOME
- POLYMER SEARCH
- Polymer Property : CTE, linear = 16.5 µm/m-°C
Polymer Property : CTE, linear = 16.5 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.5 µm/m-°C @Temperature 0.000 - 150 °C |
9.17 µin/in-°F @Temperature 32.0 - 302 °F |
X-Direction; IPC-TM-650 2.1.41 |
| Rogers Corporation XT/duroid™ 8100 0.002" Woven Glass Reinforced Thermoplastic Circuit Material XT/duroid™ 8100 woven glass reinforced thermoplastic circuit materials provide an excellent solution for printed circuit board applications used in demanding environmental conditions. XT/duroid 81.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 100 °C |
9.17 µin/in-°F @Temperature 212 °F |
|
| Outokumpu 254 SMO® High Performance Austenitic Stainless Steel Applications: Process equipment in chemical industryBleaching equipment in the pulp and paper industryFlue-gas cleaningDesalinationSeawater handlingHeat exchangersAvailable in hot rolled plate (Quar.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 200 °C |
9.17 µin/in-°F @Temperature 392 °F |
|
| Outokumpu 4436 Cr-Ni-Mo Austenitic Stainless Steel General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot r.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 200 °C |
9.17 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Industeel CLC 18.10 LN Nitrogen Containing 18Cr-10Ni Austenitic Stainless Steel Description: CLC 18.10LN is a 18Cr-10Ni austenitic stainless steel with specific Nitrogen additions. Its low carbon content avoids intergranular corrosion, even on welded pieces without an ulterior .. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 500 °C |
9.17 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Industeel URANUS® B66 High Strength Super-Austenitic Stainless Steel with PREN = 54 Description: Research carried out these last five years has shown that combined additions of chromium, tungsten, molybdenum, nitrogen and copper, make it possible to design a super-austenitic stainl.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 25 alloy, room temperature sheet after 500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 100 °C |
9.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| ATI Allegheny Ludlum Stainless Steel Chromium-Nickel-Molybdenum 317L (UNS S31703) Allegheny Ludlum's 317L™ is molybdenum-bearing austenitic stainless steel with greatly increased resistance to chemical attack as compared to the conventional chromium-nickel austenitic stainless s.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 100 °C |
9.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| ATI Allegheny Ludlum Stainless Steel Chromium-Nickel-Molybdenum 317LX™ (UNS S31725) Allegheny Ludlum's 317LX™ is molybdenum-bearing austenitic stainless steel with greatly increased resistance to chemical attack as compared to the conventional chromium-nickel austenitic stainless .. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Copyright © lookpolymers.com All Rights Reserved