Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.20 mm |
185 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Cycolac® X11 ABS Automotive: High heat resistance. Excellent flow/impact balance. UL94 HB rated. High gloss. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.20 mm |
185 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Cycoloy® RCY6214 PC+ABS (Asia Pacific) Cycoloy* RCY6214 resin is an injection moldable PC/ABS blend with non-brominated and non-chlorinated flame retardant. It contains 35% post consumer recycle content with a UL-94 V0 rating @ 1.5 mm. D.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.18 mm |
185 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
PolyOne Geon™ HTX 92052 Polyvinyl Chloride Alloy (PVC Alloy) Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.35 mm |
185 °F @Thickness 0.250 in |
Annealed; ASTM D648 |
PolyOne Geon™ HTX M6215 Polyvinyl Chloride Alloy (PVC Alloy) It is recommended that the compound pellets be dried for 3 to 4 hours at 150 deg. F.Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.18 mm |
185 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Geon™ HTX Ultra LA426G Black 2880 Polyvinyl Chloride Alloy (PVC Alloy) Higher gloss version of Geon HTX Ultra LA426Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties measured on LA426G Black 2880.Information provided by Pol.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.18 mm |
185 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
PolyOne Geon™ HTX Ultra LA436G Black 2880 Polyvinyl Chloride Alloy (PVC Alloy) Higher gloss, wider processing window version of Geon HTX Ultra LA426G.Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties measured on LA436G Black 2880... |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Cycolac® BDT6500 ABS AUTOMOTIVE. Low gloss, color concentratable for interior applications. Natural only. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
LG Chemical HF380G ABS, High Flow Feature: Injection Molding, High FlowApplication: Electric & Electronic Products)CAS No. 9003-56-9Information provided by LG Chemical |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
LG Chemical HG173 ABS, High Surface Gloss Feature: Injection Molding, High Surface GlossApplication: Electric & Electronic Products)CAS No. 9003-56-9Information provided by LG Chemical |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
LG Chemical HI100K ABS, High Impact Feature: Injection Molding, High Impact, Good ProcessingApplication: Miscellaneous Goods)CAS No. 9003-56-9Information provided by LG Chemical |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
LG Chemical HI153 ABS, High Flow Feature: Injection Molding, High Flow, Good WeatherabilityApplication: Electric & Electronic Products, Miscellaneous GoodsCAS No. 9003-56-9Information provided by LG Chemical |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 12.7 mm |
185 °F @Thickness 0.500 in |
Unannealed; ASTM-D648 |
Ineos ABS Lustran® 433 ABS, General-Purpose Injection Molding Grade Lustran® ABS 433 is a general-purpose injection molding grade of ABS (Acrylonitrile Butadiene Styrene). It is a high-impact, high-gloss ABS, available only in natural (000000) and black (904000)... |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 12.7 mm |
185 °F @Thickness 0.500 in |
Unannealed; ASTM-D648 |
Ineos ABS Lustran® 633 ABS, Injection Molding Grade Lustran® ABS 633 is a general-purpose injection molding grade of ABS (Acrylonitrile Butadiene Styrene). It offers a good balance of physical properties, high gloss, and good moldability. Typical .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
SABIC Innovative Plastics Noryl ENV85 PPE+PS (Asia Pacific) Low heat, flame retardant, extrusion grade PPO/HIPS alloy.Internal flammability results only.Not a UL recognised material.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.17 mm |
185 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
Calsak CS-72 General Purpose ABS Resin Product Characteristics:High Impact, High GlossInjection molding grade |