Thermal Properties | Metric | English | Comments |
---|---|---|---|
Glass Transition Temp, Tg | 148 °C | 298 °F | DMA; without post-cure |
Park Electrochemical Nelcote® V-376 Cyanate Ester Epoxy Prepregs, 4503 Quartz Reinforced Nelcote® V-376 is a Cyanate Ester matrix providing excellent electrical and mechanical properties for harsh aircraft, shipboard, and undersea applications for Radomes, Antenna, and Reflectors. Simp.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | DMA; without post-cure |
Park Electrochemical Nelcote® V-376 Cyanate Ester Epoxy Prepregs, 581 Quartz Reinforced Nelcote® V-376 is a Cyanate Ester matrix providing excellent electrical and mechanical properties for harsh aircraft, shipboard, and undersea applications for Radomes, Antenna, and Reflectors. Simp.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | DSC |
Gharda Chemicals GATONE™ 5300 PEEK, High Viscosity Grade
(discontinued **) High viscosity grade for extrusion and injection moldingCHARACTERISTICS: Outstanding chemical resistance.Outstanding wear resistance.Outstanding resistance to hydrolysis.Excellent mechanical propert.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | DSC |
Gharda Chemicals GATONE™ PEEK, 30% Carbon Fiber Reinforced
(discontinued **) GATONE™ PEEK grades with carbon fiber reinforcements ranging from 10- 40 % are available in natural or desired color. Custom made grades can be developed to meet specific requirements.CHARACTERISTI.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | ASTM D3482 |
Gharda Chemicals GATONE™ 5700 Polyetheretherketone (PEEK)
(discontinued **) Characteristics: Outstanding Chemical Resistance Outstanding Wear Resistance Outstanding Resistance to HydrolysisExcellent Mechanical Properties Outstanding Thermal properties Very good Dielectric.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | ASTM D3482 |
Gharda Chemicals GATONE™ 5630GF Polyetheretherketone (PEEK)
(discontinued **) Characteristics: Outstanding Chemical Resistance Outstanding Wear Resistance Outstanding Resistance to HydrolysisExcellent Mechanical Properties Outstanding Thermal properties Very good Dielectric.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | ASTM D3482 |
Gharda Chemicals GATONE™ 5330FC Polyetheretherketone (PEEK)
(discontinued **) Characteristics: Outstanding Chemical Resistance Outstanding Wear Resistance Outstanding Resistance to HydrolysisExcellent Mechanical Properties Outstanding Thermal properties Very good Dielectric.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | ASTM D3482 |
Gharda Chemicals GATONE™ 5630FC Polyetheretherketone (PEEK)
(discontinued **) Characteristics: Outstanding Chemical Resistance Outstanding Wear Resistance Outstanding Resistance to HydrolysisExcellent Mechanical Properties Outstanding Thermal properties Very good Dielectric.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | DMA; without post-cure |
Park Electrochemical Nelcote® V-376 Cyanate Ester Epoxy Prepregs, 7781 E-Glass Reinforced Nelcote® V-376 is a Cyanate Ester matrix providing excellent electrical and mechanical properties for harsh aircraft, shipboard, and undersea applications for Radomes, Antenna, and Reflectors. Simp.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | ISO 11357-1/-2 |
Covestro Makrolon® 1804 Polycarbonate MVR (300 °C/1.2 kg) 6.0 cm3/10 minhigh viscosityUV stabilizedoptimized for low plate-outimproved flammabilityUL 94 V-2/1.5 mm and 3.0 mmavailable in transparenttranslucent and opaque colorssolid sh.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | |
Covestro Makrolon® 2405 Polycarbonate, Injection Grade Very easy flowing injection molding grade with easy mold release, Makrolon grade 2458 for food contact applications.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was se.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | 10°C/min; ISO 11357-1,-2 |
Covestro Makrolon® 2600 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Med.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | |
Covestro Makrolon® 2658 Polycarbonate, Injection Grade Easy flowing BgVV- and FDA injection molding grade with easy mold release, for food contact applications, better resistance to hot water.Information provided by Bayer.As of 1 September 2015, Bayer M.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | 10°C/min; ISO 11357-1,-2 |
Covestro Makrolon® 2800 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Med.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | |
Covestro Makrolon® 2805 Polycarbonate, Injection Grade Medium flowing injection molding grade with easy mold release, Makrolon grade 2858 for food contact applications.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separ.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | ISO 11357-1/-2 |
Covestro Makrolon® 2806 Polycarbonate ISO 7391-PC,M,(,,)-09-9MVR (300 °C/1.2 kg) 9.5 cm3/10 minFood contact qualityMedium viscosityGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CAvailable in transparenttran.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | |
Covestro Makrolon® 2808 Polycarbonate, Injection Grade Medium flowing BgVV- and FDA injection molding grade, for food contact applications, better resistance to hot water.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was se.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | ISO 11357-1/-2 |
Covestro Makrolon® 3103 MAS157 Polycarbonate ISO 7391-PC,EL,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minExtrusionHigh viscosityUV stabilizedAvailable in color code 550115 onlySolid sheetCorrugated sheetPreprocessingMax. Water conte.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | |
Covestro Makrolon® 3103 Polycarbonate Injection molding and extrusion grade with high viscosity, UV stabilized, special grade for sheets.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Baye.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | |
Covestro Makrolon® 3208 Polycarbonate Injection molding and extrusion grade with high viscosity, BgVV- and FDA grade for food contact applications, yields especially tough parts, better resistance to hot water.Information provided by Ba.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | |
Covestro Makrolon® 6385 Polycarbonate, Injection Grade Low viscosity, flame retardant injection molding grade with easy mold release, not available in transparent colors.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was sep.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | |
Covestro Makrolon® 6557 Polycarbonate, Injection Grade Medium viscosity, flame retardant injection molding grade with easy mold release, UV-stabilized.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer A.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | |
Covestro Makrolon® 8025 Polycarbonate High viscosity extrusion and injection molding grade with 20% short glass fibers and easy mold release, low anisotropy, for stiff moldings requiring good dimensional stability.Information provided b.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | |
Covestro Makrolon® 8325 Polycarbonate High viscosity injection molding and extrusion grade with 20% standard glass fibers and easy mold release, high strength and stiffness.Information provided by Bayer.As of 1 September 2015, Bayer Mat.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | |
Covestro Makrolon® 8345 Polycarbonate High viscosity injection molding and extrusion grade with 35% standard glass fibers and easy mold release, stiff flow, especially high strength and stiffness.Information provided by Bayer.As of 1 Se.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | |
Covestro Makrolon® 9125 Polycarbonate Medium viscosity, flame retardant extrusion and injection molding grade with 20% standard glass fibers and easy mold release agent.Information provided by Bayer.As of 1 September 2015, Bayer Materia.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | |
Covestro Makrolon® 9415(Z) Polycarbonate Medium viscosity, flame retardant extrusion and injection molding grade with 10% standard glass fibers and easy mold release agent.Information provided by Bayer.As of 1 September 2015, Bayer Materia.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | |
Covestro Makrolon® LQ 2647 Polycarbonate, UV-Stabilized UV-stabilized injection molding grade with easy mold release, suitable for spectacle glasses (LQ = Lens Quality).Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separ.. |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | ISO 11357-1/-2 |
Covestro Makrolon® LTG3123 Polycarbonate PreprocessingMax. Water content |
|||
Glass Transition Temp, Tg | 148 °C | 298 °F | ASTM D3482 |
Gharda Chemicals GATONE™ 5330CF Polyetheretherketone (PEEK)
(discontinued **) Characteristics: Outstanding Chemical Resistance Outstanding Wear Resistance Outstanding Resistance to HydrolysisExcellent Mechanical Properties Outstanding Thermal properties Very good Dielectric.. |