Thermal Properties | Metric | English | Comments |
---|---|---|---|
Specific Heat Capacity | 0.523 J/g-°C @Temperature 20.0 °C |
0.125 BTU/lb-°F @Temperature 68.0 °F |
|
Hoskins Manufacturing Alumel® Thermocouple Wire Type K - Std All values may vary dependent on specific design and usageAlumel® is a registered trade name of Hoskins Manufacturing.Capabilities: WireRibbonSquareInsulatedPlatedInformation provided by Californ.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 600 °C |
0.125 BTU/lb-°F @Temperature 1110 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 600 °C |
0.125 BTU/lb-°F @Temperature 1110 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 600 °C |
0.125 BTU/lb-°F @Temperature 1110 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 600 °C |
0.125 BTU/lb-°F @Temperature 1110 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 600 °C |
0.125 BTU/lb-°F @Temperature 1110 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 600 °C |
0.125 BTU/lb-°F @Temperature 1110 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 600 °C |
0.125 BTU/lb-°F @Temperature 1110 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 600 °C |
0.125 BTU/lb-°F @Temperature 1110 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 600 °C |
0.125 BTU/lb-°F @Temperature 1110 °F |
|
Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 600 °C |
0.125 BTU/lb-°F @Temperature 1110 °F |
|
Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 600 °C |
0.125 BTU/lb-°F @Temperature 1110 °F |
|
Haynes 188 alloy, plate at RT after 4000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Specific Heat Capacity | 0.522 J/g-°C @Temperature 300 °C |
0.125 BTU/lb-°F @Temperature 572 °F |
|
Haynes HR-120® alloy, solution heat-treated Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Specific Heat Capacity | 0.522 J/g-°C @Temperature 300 °C |
0.125 BTU/lb-°F @Temperature 572 °F |
|
Haynes HR-120® alloy, solution heat-treated aged at 1400°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Specific Heat Capacity | 0.522 J/g-°C @Temperature 300 °C |
0.125 BTU/lb-°F @Temperature 572 °F |
|
Haynes HR-120® alloy, solution heat-treated aged at 1600°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 600 °C |
0.125 BTU/lb-°F @Temperature 1110 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
Haynes 556® alloy, bar after 16000 hours at 537°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
Haynes 556® alloy, bar after 16000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
Haynes 556® alloy, bar, after 4000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
Haynes 556® alloy, cold rolled, solution annealed sheet, 0.8-2.8 mm thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
Haynes 556® alloy, sheet after 1000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 20.0 °C |
0.125 BTU/lb-°F @Temperature 68.0 °F |
|
California Fine Wire NIFE 5200 Nickel Iron Resistance Wire All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.523 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |