Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 37.2 MPa @Temperature 93.3 °C |
5400 psi @Temperature 200 °F |
Short-Beam, Dry; ASTM D2344 |
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 120 E-Glass Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle.. |
|||
Shear Strength | 37.2 MPa @Temperature 21.1 °C |
5400 psi @Temperature 70.0 °F |
Short-Beam, Wet; ASTM D2344 |
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 285 Kevlar® Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle.. |
|||
Shear Strength | 37.2 MPa @Temperature 175 °C |
5400 psi @Temperature 347 °F |
Laminate property; In Line Shear; Conditioning: 158°F 85% RH sat |
Hexcel® HexFlow® RTM651 One-part Modified BMI Resin HexFlow® RTM651 is a one-component modified bismaleimide for resin transfer molding (RTM). Upon heating to 212-248°F, the resin will become a low viscosity homogeneous liquid that has a long pot-l.. |
|||
Shear Strength | 37.2 MPa @Temperature 163 °C |
5400 psi @Temperature 325 °F |
Short Beam, Wet (Immersed in water at 71°C for 7 days) |
Hexcel® HexPly® 954-2A Curing Cyanate Resin, Quartz Fiber Reinforced 8 Harness Satin Fabric Information provided by HexCel |
|||
Shear Strength | 37.2 MPa @Temperature 204 °C |
5400 psi @Temperature 399 °F |
Short Beam |
Hexcel® HexPly® 954-2A Curing Cyanate Resin, S-2 Glass Fiber Reinforced 8 Harness Satin Fabric Information provided by HexCel |
|||
Shear Strength | 37.2 MPa @Temperature 149 °C |
5400 psi @Temperature 300 °F |
Short Beam, Wet |
Hexcel® HexPly® 954-2A Curing Cyanate Resin, S-2 Glass Fiber Reinforced 8 Harness Satin Fabric Information provided by HexCel |
|||
Shear Strength | 37.2 MPa @Temperature 21.1 °C |
5400 psi @Temperature 70.0 °F |
Lap Shear |
Hexcel® Redux® 312 Modified epoxy film adhesive (0.015 psf) Redux® 312 is a high-strength 250°F curing film adhesive, suitable for metal to metal bonding and sandwich constructions, where operating temperatures of up to 210°F may be experienced. A support.. |
|||
Shear Strength | 37.2 MPa @Temperature 21.1 °C |
5400 psi @Temperature 70.0 °F |
Single Lap Shear (Metal/Metal), 0.03 psf, No conditioning |
Hexcel® Redux® 330M Epoxy film adhesives for the bonding and finishing of composites Redux 330 is a 350°F curing tough film adhesive which is ideally suited to structural bonding, composite to composite bonding, surface finishing, electromagnetic shielding and lightning strike appl.. |
|||
Shear Strength | 37.2 MPa @Temperature 21.1 °C |
5400 psi @Temperature 70.0 °F |
Tensile Shear, Redux 775 film |
Hexcel® Redux® 775 Vinyl phenolic structural adhesive Redux 775 was adopted as the world's first metal-to-metal bonding process to be officially approved for use in the manufacture of aircraft primary structures in 1943. It is available either as a fil.. |