Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 8.00 - 12.0 GPa | 1160 - 1740 ksi | Injection and Compression; ISO 178 |
Raschig Group 2567 AMC Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and .. |
|||
Flexural Modulus | 8.00 - 12.0 GPa | 1160 - 1740 ksi | Compression; ISO 178 |
Raschig Group 2568 AMC Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s.. |
|||
Flexural Modulus | 8.00 - 12.0 GPa | 1160 - 1740 ksi | Compression; ISO 178 |
Raschig Group 5553 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Flexural Modulus | 10.0 - 12.0 GPa | 1450 - 1740 ksi | Injection; ISO 178 |
Raschig Group MELOPAS® 156 MF Melamine Glass fiber reinforced Melamine molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 200.. |
|||
Flexural Modulus | 8.00 - 12.0 GPa | 1160 - 1740 ksi | Injection and Compression; ISO 178 |
Raschig Group RALUPOL® 4802 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u.. |
|||
Flexural Modulus | 8.00 - 12.0 GPa | 1160 - 1740 ksi | Injection and Compression; ISO 178 |
Raschig Group RALUPOL® 802 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength, good heat resistance. This product meets the allowed up.. |
|||
Flexural Modulus | 8.00 - 12.0 GPa | 1160 - 1740 ksi | Injection and Compression; ISO 178 |
Raschig Group RALUPOL® 804 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy m.. |
|||
Flexural Modulus | 9.10 - 12.0 GPa | 1320 - 1740 ksi | Average value: 10.2 GPa Grade Count:6 |
Overview of materials for Liquid Crystal Polymer (LCP), Unfilled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Unfilled". Each property range of values reported is minimum and maximum v.. |
|||
Flexural Modulus | 2.70 - 12.0 GPa | 392 - 1740 ksi | Average value: 4.45 GPa Grade Count:6 |
Overview of materials for Nylon 6-3 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6-3". Each property range of values reported is minimum and maximum values of appropriate MatWeb e.. |
|||
Flexural Modulus | 1.65 - 12.0 GPa | 239 - 1740 ksi | Average value: 4.05 GPa Grade Count:5 |
Overview of materials for Nylon, Amorphous Transparent Alloy This property data is a summary of similar materials in the MatWeb database for the category "Nylon, Amorphous Transparent Alloy". Each property range of values reported is minimum and maximum value.. |
|||
Flexural Modulus | 10.0 - 12.0 GPa | 1450 - 1740 ksi | ISO 178 |
Bulk Molding Compounds tetra-DUR F 4209 Bulk Molding Compound Highest Arc resistanceTypical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipation (explosion protection), therm.. |
|||
Flexural Modulus | 8.00 - 12.0 GPa | 1160 - 1740 ksi | ISO 178 |
Bulk Molding Compounds tetra-DUR F 4308 Bulk Molding Compound UL-licensedTypical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipation (explosion protection), thermal stabilit.. |
|||
Flexural Modulus | 9.00 - 12.0 GPa | 1310 - 1740 ksi | ISO 178 |
Bulk Molding Compounds tetra-DUR N 4111 Bulk Molding Compound Smooth, high gloss surface. Low profile.Typical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipation (explosion.. |
|||
Flexural Modulus | 8.00 - 12.0 GPa | 1160 - 1740 ksi | Compression; ISO 178 |
Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl phthalate molding compound free from halogens. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exc.. |
|||
Flexural Modulus | 10.0 - 12.0 GPa | 1450 - 1740 ksi | ISO 178 |
Vyncolit 3520 CG Novolac Phenolic Graphite filled phenolic molding compound with excellent dimensional stability. Self-lubricating and has a low coefficient of friction. Not suitable for electrical applications.USES: Gas meter par.. |
|||
Flexural Modulus | 3.20 - 12.0 GPa | 464 - 1740 ksi | Average value: 5.51 GPa Grade Count:12 |
Overview of materials for Polyphenylene Sulfide (PPS), Unreinforced, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Unreinforced, Extruded". Each property range of values reported is minimum .. |
|||
Flexural Modulus | 9.00 - 12.0 GPa | 1310 - 1740 ksi | ISO 178 |
Bulk Molding Compounds tetra-DUR F 4206 Bulk Molding Compound General purpose productTypical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipation (explosion protection), ther.. |