Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 2.87 GPa | 416 ksi | ASTM D790 |
PolyOne Geon™ Vinyl Rigid Extrusion L0111 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
Flexural Modulus | 2.87 GPa | 416 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics EXTEM XH1015 TPI Resin Thermoplastic Polyimide Extem* XH1015 Resin. |
|||
Flexural Modulus | 2.87 GPa | 416 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics EXTEM XH1015 TPI Resin (Asia Pacific) Thermoplastic Polyimide Extem* XH1015 Resin. |
|||
Flexural Modulus | 2.87 GPa | 416 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics EXTEM XH1015 TPI Resin (Europe-Africa-Middle East) Thermoplastic Polyimide Extem* XH1015 Resin. |
|||
Flexural Modulus | 2.87 GPa | 416 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics EXTEM XH1015F TPI Resin (Europe-Africa-Middle East) Thermoplastic Polyimide Extem* XH1015 Resin. EFSA food Contact approved. |
|||
Flexural Modulus | 2.87 GPa | 416 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP IFL21 PA6.12 LNP LUBRICOMP* IFL21 is a compound based on Nylon 6/12 resin containing 5% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant. |
|||
Flexural Modulus | 2.87 GPa | 416 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP MF002S PP LNP* Thermocomp* MF002S is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Modulus | 2.87 GPa | 416 ksi | ASTM D-790 |
CMT Materials REN Shape® 472 Machinable Board for Prototype Tooling & Assembly Fixtures RenShape 472 is a polyurethane-based board designed for CNC machining of production grade checking and assembly fixtures. It may also be used in prototype thermoforming and vacuum forming tooling a.. |