Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 4.72 GPa | 685 ksi | ASTM D790 |
Polymer Resources NY66-G13 Nylon 66, 13% Glass Reinforced Nylon 66, 13% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are test.. |
|||
Flexural Modulus | 4.72 GPa | 685 ksi | ASTM D790 |
Polymer Resources NY66-G13-[color]-H Nylon 66, 13% Glass Reinforced, Heat Stabilized Nylon 66, 13% Glass Reinforced, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylo.. |
|||
Flexural Modulus | 4.72 GPa | 685 ksi | ASTM D790 |
Polymer Resources NY66-G13-[color]H Nylon, 13% Glass Reinforced, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
Flexural Modulus | 4.72 GPa | 685 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP KFL32L Acetal Copolymer LNP* LUBRICOMP* KFL32L is a compound based on Acetal Copolymer resin containing 10% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant. |
|||
Flexural Modulus | 4.72 GPa | 685 ksi | ASTM D 790 |
SABIC Innovative Plastics LNP Lubricomp KFL32L Acetal Copolymer (Asia Pacific) LNP* Lubricomp* KFL32L is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.This data was supp.. |
|||
Flexural Modulus | 4.72 GPa | 685 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP SX93441D PA12 LNP* Lubricomp* SX93441D is a compound based on Nylon 12 containing Proprietary Fillers. Characteristics of this grade are: Internally Lubricated. |
|||
Flexural Modulus | 4.72 GPa | 685 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Lubricomp SX93441D PA6.12 LNP* Lubricomp* SX93441D is a compound based on Nylon 6/12 containing Proprietary Fillers. Characteristics of this grade are: Internally Lubricated.This data was supplied by SABIC-IP for the Ameri.. |
|||
Flexural Modulus | 4.72 GPa | 685 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp GF003 PSU LNP THERMOCOMP* GF003 is a compound based on Polysulfone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 4.72 GPa | 685 ksi | ASTM D790 |
Teknor Apex Beetle® 140 BH Nylon 66, Glass Bead Reinforced Processing Method: Injection Molding Forms: PelletsInformation Provided by Teknor Apex |
|||
Flexural Modulus | 4.72 GPa | 685 ksi | ASTM D790 |
SABIC Innovative Plastics NORYL PX4716 PPE+HIPS (Asia Pacific) PPE+PS GF15% FR V-1 |
|||
Flexural Modulus | 4.72 GPa | 684 ksi | ASTM D790 |
A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT Information provided by A. Schulman. |
|||
Flexural Modulus | 4.72 GPa | 684 ksi | ASTM D790 |
A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT Information provided by A. Schulman. |
|||
Flexural Modulus | 4.72 GPa | 684 ksi | ASTM D790 |
A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT Information provided by A. Schulman. |
|||
Flexural Modulus | 4.72 GPa | 684 ksi | ASTM D790 |
A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT Information provided by A. Schulman. |
|||
Flexural Modulus | 4.72 GPa | 684 ksi | ASTM D790 |
A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT Information provided by A. Schulman. |
|||
Flexural Modulus | 4.72 GPa | 684 ksi | ASTM D790 |
A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT Information provided by A. Schulman. |
|||
Flexural Modulus | 4.72 GPa | 685 ksi | ASTM-D-790 |
BCC Products MB 5000 Urethane Tooling Board MB 5000 is an extremely tough, high impact Urethane Plank, that can be used for metal forming as well as nickel plating mandrels. Features: excellent machinability, low dust emission, mostly shavin.. |