Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 3.65 GPa | 529 ksi | |
Plastcom SLOVAMID 66 C 15 MI PA66, 15% mineral filling Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.0.. |
|||
Flexural Modulus | 3.65 GPa | 529 ksi | |
Plastcom SLOVAMID 66 T 15 MI PA66, 15% mineral filling FeaturesPA 66 with the content of 15 % chemically modified mineral filling and impact modified. Used for holders of electric hand tools, for hobby tools, gears, covers of electric tools, flat produc.. |
|||
Flexural Modulus | 3.65 GPa | 529 ksi | ASTM D790 |
Polymer Resources PPX-G10HF Modified-PPO, 10% Glass Reinforced, High Flow Modified-Polyphenylene Oxide, 10% Glass Reinforced, High FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inf.. |
|||
Flexural Modulus | 3.65 GPa | 530 ksi | Resin |
Renegade Materials Corporation RM-5003 Cyanate Ester Prepreg 4581 Quartz Fabric Low dielectric and loss, high performance prepreg. 350°F Cure Developed with consistent handling and superior performance Designed for demanding electrical, radome and antennae applications Del.. |
|||
Flexural Modulus | 3.65 GPa | 530 ksi | Tangent; ASTM D790 |
Fiberfil® PP-60/TC/40 Polypropylene Homopolymer, 40% Talc Filled Information provided by FIBERFIL Engineered Plastics |
|||
Flexural Modulus | 3.65 GPa | 529 ksi | ISO 178 |
Solvay TECHNYL® B 50 H1 PA66/6, DRY Description: TECHNYL® B 50H1 is an unreinforced melamine cyanurate flame retarded copolyamide 66/6. This product has been heat stabilized and is suitable for injection molding. This product is av.. |
|||
Flexural Modulus | 3.65 GPa | 529 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP ZFL31XXC PPE+PS LNP* LUBRICOMP* ZFL31XXC is a compound based on PPE+PS resin containing 5% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant |
|||
Flexural Modulus | 3.65 GPa | 530 ksi | ASTM D790 |
Techmer ES Electrablend® PA6/6 IM C BK Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/Reinfor.Additive: Impact ModifierFeatures: Conductive and Impact ModifiedAppearance: BlackInformation provided by TP.. |
|||
Flexural Modulus | 3.65 GPa | 530 ksi | secant; ASTM D790 |
Spartech PP5420 Glass Fiber Reinforced Homopolymer Provides the maximum strength and heat resistance among polypropylene compounds. Physical properties can approach those of more expensive engineering resins.Information provided by Spartech |
|||
Flexural Modulus | 3.65 GPa | 530 ksi | ASTM D790 |
Techmer ES HiFill® PA6/6 GF6 HS BK 6% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 6% Filler by WeighAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedAppearance:.. |
|||
Flexural Modulus | 3.65 GPa | 530 ksi | ASTM D790 |
Techmer ES Luriblend® PA6 GL15 Nylon 6 Availability: North AmericaForms: PelletsAdditive: Graphite Powder Lubricant(15%)Features: LubricatedInformation provided by TP Composites, Inc. |
|||
Flexural Modulus | 3.65 GPa | 530 ksi | 0.125 in, injection molded, unannealed; ASTM D790 |
Styron EMERGEâ„¢ 4731-8 Polycarbonate EMERGEâ„¢ PC 4702-15 advanced resin is formulated with 10% glass fiber and has an f1 rating by Underwriters Laboratories Inc. It provides good ignition resistance, rigidity, dimension stability .. |
|||
Flexural Modulus | 3.65 GPa | 529 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® SHF4910 PBT (Europe-Africa-Middle East) 6.5% glass reinforced, Super High Flow, flame retardant PBT. |
|||
Flexural Modulus | 3.65 GPa | 529 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® SHF4910 PBT (Europe-Africa-Middle East) 6.5% glass reinforced, Super High Flow, flame retardant PBT. |
|||
Flexural Modulus | 3.65 GPa | 529 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP NF001 PC+ABS (Asia Pacific) LNP* Thermocomp* NF001 is a compound based on PC+ABS Blend resin containing Glass Fiber. |
|||
Flexural Modulus | 3.65 GPa @Temperature 22.8 °C |
530 ksi @Temperature 73.0 °F |
ASTM D790 |
Ensinger Tecapeek® Polyetheretherketone (PEEK) TECAPEEK™ high performance polymer, made from Victrex PEEK polymer, has successfully replaced glass, stainless steel and titanium in a growing range of medical applications. The material's excepti.. |
|||
Flexural Modulus | 3.65 GPa | 530 ksi | ASTM D790 |
Asahi Kasei Thermylene® P6-20FG-0153 20% Glass Fiber Reinforced, UV Stable Information provided by Asahi Thermofil |
|||
Flexural Modulus | 3.65 GPa | 530 ksi | ASTM D790 |
Asahi Kasei Thermylene® P6-30FG-0877A 30% Glass Fiber Reinforced, UV Stabilized Information provided by Asahi Thermofil |
|||
Flexural Modulus | 3.65 - 5.03 GPa | 530 - 730 ksi | |
Bulk Molding Compounds BMC T60 Grey Wear Resistant Molding Compound BMC T60 Grey is a wear resistant molding compound specifically formulated for applications that require excellent abrasion resistance. Due to its low specific gravity it has substantial cost per cu.. |
|||
Flexural Modulus | 3.65 GPa | 530 ksi | ASTM D790 |
Asahi Kasei Thermylene® P6-40FB-Y947 40% Glass Fiber/Glass Bead, Heat Stabilized Information provided by Asahi Thermofil |
|||
Flexural Modulus | 3.65 GPa | 530 ksi | ASTM D790 |
ScanTube PEEK Tubing Information provided by ScanTube, Inc. |
|||
Flexural Modulus | 3.65 - 11.4 GPa | 530 - 1650 ksi | Average value: 9.18 GPa Grade Count:50 |
Overview of materials for Polyethylene Terephthalate (PET), 30% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 30% Glass Reinforced". Specific grades with glass content between 25% .. |
|||
Flexural Modulus | 3.65 - 5.03 GPa | 530 - 730 ksi | |
Bulk Molding Compounds BMC T60-6006 Wear Resistant Molding Compound BMC T60-6006 is a wear resistant molding compound specifically formulated for applications that require excellent abrasion resistance. Due to its low specific gravity it has substantial cost per cu.. |