Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 14.7 GPa | 2130 ksi | ISO 178 |
Nilit FRIANYL A63 GV50 Nylon 6.6 for injection molding, 50% glass fiber reinforced Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 14.7 GPa | 2130 ksi | ISO 178 |
Nilit FRIANYL A63 H-GV50 Nylon 6.6 for injection molding, 50% glass fiber reinforced Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 14.7 GPa | 2130 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 |
Fibre Glast Epolite 2427 Epoxy
(discontinued **) Information provided by Fibre Glast Developments Corporation. |
|||
Flexural Modulus | 14.7 GPa | 2130 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP LCL33 PEEK LNP* LUBRICOMP* LCL33 is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Wear Resistant. |
|||
Flexural Modulus | 14.7 GPa | 2130 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP LCL33E PEEK LNP LUBRICOMP* LCL33E is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Easy Molding, Wear Resistant. |
|||
Flexural Modulus | 14.7 GPa | 2130 ksi | ISO 178 |
Solvay Specialty Polymers Amodel® FC-1140 Polyphthalamide (PPA), 40% Glass Fiber Amodel® FC-1140 is an FDA-approved, 40% glass fiber reinforced resin designed for high strength and stiffness. This combines with its excellent thermal properties, low water absorption and good h.. |
|||
Flexural Modulus | 14.7 GPa | 2130 ksi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® XP-2150IM PPS, 50% Glass Reinforced PPS/GS that is used in mobile phone LCD bracketInformation provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 14.7 GPa | 2130 ksi | ASTM D790 |
Sumitomo Bakelite North America SI 9041A Silicone Compound SI 9041A is a long fiberglass reinforced silicone molding compound, which exhibits excellent high temperature properties in addition to good molding characteristics for transfer and compression mold.. |
|||
Flexural Modulus | 14.7 GPa | 2130 ksi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® XP-2150IM PPS, 50% Glass Reinforced PPS/GS that is used in mobile phone LCD bracketInformation provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 14.7 GPa | 2130 ksi | ISO 178 |
Unitika E-RUNG60 PA66, 60% Glass Fiber Reinforced, Conditioned Information provided by Unitika Ltd. |
|||
Flexural Modulus | 14.7 GPa | 2130 ksi | ASMT D790 |
Toyobo TS501 PPS, 50% Glass Fiber Reinforced Key Feature: High stiffnessHigh performance injection-molding resin created from crystalline polyphenylene sulfide, using a special formulation technology developed by Toyobo. Excellent physical, e.. |
|||
Flexural Modulus | 14.7 GPa | 2130 ksi | ASTM D790 |
Ensinger Tecapeek® XP-98ST Compression Molded PEEK ST, 30% Carbon Fiber Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in.. |
|||
Flexural Modulus | 14.7 GPa | 2130 ksi | ASTM D790 |
A. Schulman ComAlloy Hiloy® 435 Glass/Mineral Reinforced, PBT Alloy Data provided by the manufacturer, ComAlloy International Company.50% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |