Polymer Property : Flexural Modulus = 0.689 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	0.689 GPa	100 ksi	1.3 mm/min; ASTM D790B
Polimeros Mexicanos Rotolene® 93050 Medium Density Polyethylene Hexene Copolymer Linear Medium Density Polyethylene for rotational molding. This resin is fully UV8 stabilized.Recommended for general purpose applications. Frequently used for water tanks (less tha..
Flexural Modulus	0.689 GPa	100 ksi	1.3 mm/min; ASTM D790B
Polimeros Mexicanos Rotolene® Diesel Tank Medium Density Polyethylene Hexene Copolymer Linear Medium Density Polyethylene. This resin is fully UV8 stabilized.High quality Polyethylene compound specially designed for automotive applications, water tanks, diesel tanks a..
Flexural Modulus	0.689 GPa	100 ksi	ASTM D790
Network Polymers NPP 11-0535 Description: Linear Low Density Polyethylene (LLDP)Information provided by Network Polymers Inc.
Flexural Modulus	0.689 GPa	100 ksi	1.3mm per min; ASTM D790
Formosa Plastics Formolene® L63550U Rotational Molding LLDPE (discontinued **) Hexene CopolymerApplications: Toys, medium tanks, material handling equipment and flat surface rotational molding applications.Formolene L63550 is fully heat and UV stabilized.Meets all requirements..
Flexural Modulus	0.689 GPa	100 ksi	1.3mm per min; ASTM D790
Formosa Plastics Formolene® L63565U Rotational Molding LLDPE (discontinued **) Hexene CopolymerApplications: Toys, medium tanks, material handling equipment and flat surface rotational molding applications.Formolene L63565U is fully heat and UV stabilized.Meets all requirement..
Flexural Modulus	0.689 GPa	100 ksi	2% Secant - Method 1; ASTM D790
Ineos K38-20-188 HDPE K38-20-188 is a natural, UV stabilized, medium density polyethylene resin designed specifically for use with an approved Ineos North America yellow masterbatch to produce pipe or tubing for natural ..
Flexural Modulus	0.689 GPa	100 ksi	Tangent, 0.5 in/min; ASTM D790
LyondellBasell Hifaxâ„¢ EP2015/60 Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ EP2015/60 medium melt flow, 690 MPa flexural modulus, extrusion coating grade, specialty polypropylene copolymer has a very good balance of properties and processability. Th..
Flexural Modulus	0.689 GPa	100 ksi	ASTM D790
Techmer ES ElastoblendÂ® PA6 IM 835 HS L Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impact Modified and LubricatedProcessing Method: Injection MoldingInformat..
Flexural Modulus	0.689 GPa	100 ksi	ASTM D790
A. Schulman POLYTROPE™ TPP 1010-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristics ..
Flexural Modulus	0.689 GPa	100 ksi	ASTM D790
A. Schulman POLYTROPE™ TPP 1010HF-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010HF-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristic..
Flexural Modulus	0.689 GPa	100 ksi	ASTM D790
A. Schulman POLYTROPE™ TPP 510 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 510 is an injection molding grade olefinic thermoplastic elastomer. This product has excellent low temperature impact properties and flow characteristics suitable for moldi..
Flexural Modulus	0.689 GPa	100 ksi	at 1% secant; ASTM D790
A. Schulman SCHULINK® X XL350 Cross-Linkable, High Density Polyethylene DescriptionSchuLink XL 350 is a cross-linkable, high density polyethylene used from rotational molding. This resin offers high impact strength, good abrasion resistance, good stiffness, and excelle..
Flexural Modulus	0.689 GPa	100 ksi	at 1% secant; ASTM D790
A. Schulman SCHULINK® X XL350 Cross-Linkable, High Density Polyethylene DescriptionSchuLink XL 350 is a cross-linkable, high density polyethylene used from rotational molding. This resin offers high impact strength, good abrasion resistance, good stiffness, and excelle..
Flexural Modulus	0.689 GPa	100 ksi	ASTM D790
A. Schulman POLYTROPE™ TPP 1010HF-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010HF-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristic..
Flexural Modulus	0.689 GPa	100 ksi	ASTM D790
A. Schulman POLYTROPE™ CB 1010U-330 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope CB 1010U-330 is a color matched/color blended injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properti..
Flexural Modulus	0.689 GPa	100 ksi	ASTM D790
A. Schulman POLYTROPE™ TPP 1010E-01 Olefinic Elastomer For Sheet Extrusion DescriptionPolytrope TPP 1010E-01 is an olefinic elastomer designed for sheet extrusion, profile extrusion and blow molding. TPP 1010E-01 is a natural product which can be colored and UV stabilized..
Flexural Modulus	0.689 GPa	100 ksi	ASTM D790
A. Schulman POLYTROPE™ TPP 1010HF-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010HF-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristic..
Flexural Modulus	0.689 GPa	100 ksi	ASTM D790
A. Schulman POLYTROPE™ TPP 1010E-01 Olefinic Elastomer For Sheet Extrusion DescriptionPolytrope TPP 1010E-01 is an olefinic elastomer designed for sheet extrusion, profile extrusion and blow molding. TPP 1010E-01 is a natural product which can be colored and UV stabilized..
Flexural Modulus	0.689 GPa	100 ksi	0.05 in/min; ISO 178
CTC X-PRO CTC PP 4025 Polypropylene Copolymer X-PRO PP 4025 is a high value polypropylene copolymer. It has applications in general purpose industrial, housewares, and construction.Data provided by Composite Technologies (CTC).
Flexural Modulus	0.689 GPa	100 ksi	Compression molded parts prepared according to ASTM D 1928, method 1, procedure B.; ASTM D790
Dow DFDC-7525 NT High Density Polyethylene Resin DOW DFDC-7525 NT is produced using UNIPOL™ process technology. It is intended for use in thin wall drip tape and micro-irrigation tube, hose and tube, and profile extrusion applications. Informati..
Flexural Modulus	0.689 GPa	100 ksi	ASTM D790
Multibase Multi-Flam™ 0107 HDPE Polyethylene Features:Flame RetardantHalogen Content, Low to None Forms:PelletsProcessing Methods:Injection MoldingCoextrusionExtrusionUses:TubingPipingInformation provided by Multibase
Flexural Modulus	0.689 GPa	100 ksi	ASTM D790
A. Schulman POLYTROPE™ TPP 510 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 510 is an injection molding grade olefinic thermoplastic elastomer. This product has excellent low temperature impact properties and flow characteristics suitable for moldi..
Flexural Modulus	0.689 - 2.45 GPa	99.9 - 355 ksi	Average value: 1.19 GPa Grade Count:65
Overview of materials for Polypropylene, Blow Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Blow Molding Grade". Each property range of values reported is minimum and maximum values..