Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Creep Modulus, 1000 hours | 1900 - 9600 MPa | 276000 - 1.39e+6 psi | Average value: 5430 MPa Grade Count:3 |
Overview of materials for Polycarbonate, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 20% Glass Filled". Specific grades with glass content between 15% and 24% are included. E.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® 1239 Polycarbonate, Blow Molding/Extrusion Grade
(discontinued **) Pseudoplastic behavior and high viscosity extrusion and injection molding grade, BgVV- and FDA grade for food contact applications, high melt stability, better resistance to hot water, specially sui.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 1952 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardancy• Me.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® 2405 Polycarbonate, Injection Grade Very easy flowing injection molding grade with easy mold release, Makrolon grade 2458 for food contact applications.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was se.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2408 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medical devices - bioc.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2556 Polycarbonate MVR (300 °C/1.2 kg) 14 cm3/10 minEasy releaseGood hydrolysis resistanceInjection moldingAvailable in transparentTranslucent and opaque colorsFood contact gradePreprocessingMax. Water content |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2607 MAS167 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Med.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2656 Polycarbonate ISO 7391-PC,MR,(,,)-18-9Global gradeMVR (300 °C/1.2 kg) 12.5 cm3/10 minFood contact qualityMedium viscosityEasy releaseGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CAv.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2667 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardant• Med.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® 2803 Polycarbonate, Injection Grade Medium flowing injection molding grade with UV stabilizer.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name .. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2805 MAS145 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Med.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2805 MAS152 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Med.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® 2807 Polycarbonate, Injection Grade Medium flowing injection molding grade with easy mold release and UV stabilizer.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® 2808 Polycarbonate, Injection Grade Medium flowing BgVV- and FDA injection molding grade, for food contact applications, better resistance to hot water.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was se.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2856 Polycarbonate ISO 7391-PC,MR,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 9.5 cm3/10 minFood contact qualityMedium viscosityEasy releaseGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CAva.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 3100 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Hig.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 3152 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Food contact quality•.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 3156 Polycarbonate ISO 7391-PC,MR,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minFood contact qualityHigh viscosityEasy releaseGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CExtru.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 3206 Polycarbonate ISO 7391-PC,M,(,,)-05-9MVR (300 °C/1.2 kg) 4.0 cm3/10 minFood contact qualityHigh viscosityGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CExtrusionAvailable in transpar.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 6265 Polycarbonate, Flame Retardant Grade ISO 7391-PC,MFR,(,,)-18-9Global gradeMVR (300 °C/1.2 kg) 19 cm3/10 minFlame retardantUL 94V-0/1.5 mmLow viscosityEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable in opaque co.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® 6465 Polycarbonate, Injection Grade Medium viscosity, flame retardant injection molding with easy mold burning behavior.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and offici.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® 9425 Polycarbonate High viscosity, flame retardant extrusion and injection molding grade with 20% standard glass fibers and easy mold release agent.Information provided by Bayer.As of 1 September 2015, Bayer MaterialS.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® AL 2643 Polycarbonate, Injection Grade Easy flowing injection molding grade, UV-stabilized.Applications: Automotive lens applications, fulfills U.S. specification SAE J 576C.Information provided by Bayer.As of 1 September 2015, Bayer Mat.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 1243 Polycarbonate ISO 7391-PC,ELS,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minExtrusionHigh viscosityBranchedUV stabilizedEasy releaseAvailable in color code 550111onlyMulti wall sheet/profilesPreprocessi.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2456 Polycarbonate ISO 7391-PC,MR,(,,)-18-9Global gradeMVR (300 °C/1.2 kg) 19 cm3/10 minFood contact qualityLow viscosityEasy releaseGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CAvailab.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® ET2613 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Extrusion• Medium vi.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® ET3227 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Extrusion• High visc.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
BASF Luranyl® KR 2402 Polyphenylene Ether + Styrene-Butadiene Blend, Impact Grade Base grade with a balanced combination of impact strength and stiffness for parts calling for good heat deformation resistance (e.g. warm-air vents, coil formers, sheet and wheel covers).Data was co.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Ineos ABS NOVODUR® P2T ABS, Injection Grade
(discontinued **) Injection molding grade, very high heat resistance.Applications: Automotive industry, household appliances.Information provided by the manufacturer.Novodur is produced by Styrolution (2014). This g.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® LQ 2643 Polycarbonate, UV-Stabilized UV-stabilized injection molding grade, good flow, suitable for spectacle glasses (LQ = Lens-Quality).Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Ba.. |