Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 96.5 MPa | 14000 psi | ASTM D732 |
Quadrant EPP Ketron® GF30 PEEK, Extruded 30% Glass-Reinforced Polyetherether Ketone (ASTM Product Data Sheet) |
|||
Shear Strength | 96.5 MPa | 14000 psi | ASTM D732 |
Quantum PEEK 30% Glass Fiber Filled Information provided by Quantum Advanced Engineering Plastics |
|||
Shear Strength | 96.5 MPa | 14000 psi | |
Quadrant EPP Ketron® GF30 LSG PEEK, Extruded 30% Glass-Reinforced Polyetherether Ketone (ASTM Product Data Sheet) |
|||
Shear Strength | 96.5 MPa | 14000 psi | |
LE Phenolic Laminate Linen based phenolic provides more mechanical strength than paper grades and has a finer surface with better machinability. This material is used for gears, pinions, bearings, bushings, and many st.. |
|||
Shear Strength | 96.5 MPa | 14000 psi | |
X Phenolic Laminate Paper based phenolic provides low cost electrical and mechanical properties. It is widely used for switchboards, panel boards, insulating washers, and intricate punched parts.Information provided b.. |
|||
Shear Strength | 96.5 MPa @Thickness 3.17 mm |
14000 psi @Thickness 0.125 in |
|
Industrial Laminates/Norplex MC320LE Cotton Fabric Description: Grade MC320LE is a fine weave bleached cotton phenolic composite that has excellent machining characteristics and low moisture absorption. Applications include marine applications, term.. |
|||
Shear Strength | 96.5 MPa @Thickness 15.7 mm |
14000 psi @Thickness 0.620 in |
ASTM D732 |
Industrial Laminates/Norplex NP101 Synthetic Fabric Description: Phenolic resin combined with spun nylon fabric. Good impact strength and excellent electrical properties under high humidity conditions. Meets applicable Boeing specification, but exemp.. |
|||
Shear Strength | 96.5 MPa @Thickness 15.7 mm |
14000 psi @Thickness 0.620 in |
ASTM D732 |
Industrial Laminates/Norplex NP310 Cotton Fabric Description: Canvas machining grade for structural and mechanical applications. Better impact strength than phenolic paper grades. MIL-I-24768/16. Thickness Tested: 0.062, 0.125", and 0.500". |
|||
Shear Strength | 96.5 MPa @Thickness 15.7 mm |
14000 psi @Thickness 0.620 in |
ASTM D732 |
Industrial Laminates/Norplex NP310E Cotton Fabric Description: Manufactured with a domestic cotton fabric and phenolic resin. Similar to NP310 with improved moisture resistance and electrical properties. Mechanical properties equivalent to NP310. M.. |
|||
Shear Strength | 96.5 MPa @Thickness 15.7 mm |
14000 psi @Thickness 0.620 in |
ASTM D732 |
Industrial Laminates/Norplex NP342 Cotton Fabric Description: Fine weave canvas phenolic material with fabric construction weight intermediate to NP310 and NP320. Designed for better machining than grade NP310 and lower cost than NP320.Thickness T.. |
|||
Shear Strength | 96.5 MPa @Thickness 15.7 mm |
14000 psi @Thickness 0.620 in |
ASTM D732 |
Industrial Laminates/Norplex NP344 Cotton Fabric Description: Fine weave canvas laminate with high temperature phenolic resin and molybdenum disulfide lubricant. Good machining properties and low coefficient of thermal expansion. Better machining .. |
|||
Shear Strength | 96.5 MPa @Thickness 15.7 mm |
14000 psi @Thickness 0.620 in |
ASTM D732 |
Industrial Laminates/Norplex NP634 Laminate Description: Warm punching, composite grade with woven glass covers for improved flexural, tensile and impact strength. Electrical properties comparable to NP611.Thickness Tested: 0.062", 0.125" and.. |
|||
Shear Strength | 96.5 MPa @Thickness 15.7 mm |
14000 psi @Thickness 0.620 in |
ASTM D732 |
Industrial Laminates/Norplex NP660 Paper Base Laminate Description: Lower cost paper phenolic NEMA Grade XP. Uses natural kraft paper without pigmented cover sheet. Warm to hot punching. UL listed. Thickness Tested: 0.062", 0.125" & 0.500" |
|||
Shear Strength | 96.5 MPa | 14000 psi | ASTM D732 |
Haysite H722 Polyester, Glass Reinforced H722 is an all-purpose GPO-1 fiberglass mat reinforced thermoset polyester molded sheet. Available in thicknesses ranging from .031" - 2.00". Standard color - Natural. Meets Gov't Specs - LP-509, .. |
|||
Shear Strength | 96.5 MPa | 14000 psi | ASTM D732 |
Haysite H900 Polyester, Glass Reinforced H900 is recognized throughout the world as a reliable, consistent GPO-3 material. Standard size sheets are available in thicknesses ranging from .094" to 2.00". H900 also exhibits excellent smoke,.. |
|||
Shear Strength | 96.5 MPa | 14000 psi | ASTM D732 |
Haysite HCR-125 Vinyl Ester Sheet, Corrosion Resistant HCR-125 is a corrosion resistant vinyl ester sheet created by impregnating fiber glass mat, synthetic surface veil, and inert additives with Derkane 470 resin and catalyst. A compression molded pro.. |
|||
Shear Strength | 96.5 MPa | 14000 psi | Ultimate |
Ensinger TECAPEI® 30% Glass Reinforced, made from Ultem® 2300 PEI TECAPEI™ is an amorphous thermoplastic polyetherimide (PEI) made from Sabic Innovative Plastics' Ultem® 1000 and 2000 series resins. The unreinforced 1000 series materials are translucent amber in.. |