Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 82.7 MPa @Temperature 22.8 °C |
12000 psi @Temperature 73.0 °F |
ASTM D732 |
Quadrant EPP KETRON® MD PEEK, A Metal-Detectable Polyetheretherketone |
|||
Shear Strength | 82.7 MPa | 12000 psi | Short Beam Shear, 0° Direction, RT, Dry; ASTM D2344 |
Renegade Materials Corporation RM-5003 Cyanate Ester Prepreg 4581 Quartz Fabric Low dielectric and loss, high performance prepreg. 350°F Cure Developed with consistent handling and superior performance Designed for demanding electrical, radome and antennae applications Del.. |
|||
Shear Strength | 82.7 MPa | 12000 psi | |
Chevron Phillips Ryton® A-200 PPS Polyphenylene Sulfide
(discontinued **) Ryton® PPS is used in many electronic and automotive applications because of its high strength, favorable electrical properties, and high temperature stability.Data provided by the manufacturer.Sol.. |
|||
Shear Strength | 82.7 MPa | 12000 psi | |
XXX Phenolic Laminate Paper based phenolic provides low cost electrical and mechanical properties. It is widely used for switchboards, panel boards, insulating washers, and intricate punched parts.Information provided b.. |
|||
Shear Strength | 82.7 MPa @Thickness 15.7 mm |
12000 psi @Thickness 0.620 in |
ASTM D732 |
Industrial Laminates/Norplex NP320U Cotton Fabric Description: Utility version of NP320E. Meets most, but not all, NEMA properties for L and LE, and is not certifiable as a NEMA Grade.Thickness Tested: 0.062", 0.125", and 0.500" |
|||
Shear Strength | 82.7 MPa @Thickness 15.7 mm |
12000 psi @Thickness 0.620 in |
ASTM D732 |
Industrial Laminates/Norplex NP691 Paper Base Laminate Description: Flame resistant, room temperature punching grade. NP691 is very similar to NP612 in electrical properties and mechanical strength, with improved moisture resistance.Thickness Tested: 0... |
|||
Shear Strength | 82.7 MPa @Thickness 15.7 mm |
12000 psi @Thickness 0.620 in |
ASTM D732 |
Industrial Laminates/Norplex NP318 Cotton Fabric Description: Post-forming canvas phenolic material. Mechanical and electrical properties similar to NP310E. It is made from a cotton fabric weighing more than 4 ounces per square yard and having a t.. |
|||
Shear Strength | 82.7 - 96.5 MPa | 12000 - 14000 psi | |
SGL Carbon Group SIGRAFIL C® in 250°F Epoxy 60% fiber volumeInformation provided by SGL Carbon Group |
|||
Shear Strength | 82.7 MPa | 12000 psi | ASTM D732 |
Techmer ES Electrafil® J-1/CF/20 Nylon 66, 20% Carbon Fiber Reinforced |
|||
Shear Strength | 82.7 MPa | 12000 psi | Short Beam; ASTM D2344 |
Zyvex Performance Materials Arovex™ 250 Carbon Nanotube Strengthened Prepreg Arovex® 250 Prepreg is a 180°F (82°C) to 280°F (138°C) curing carbon nanotube strengthened epoxy prepreg suitable for numerous composites applications. Normal curing takes place at 250°F (121°.. |
|||
Shear Strength | 82.7 MPa | 12000 psi | ASTM D3846 |
CIP Composites 100 Series Laminated Polymer Bearing Material The 100 series consists of polyester fabric and one of several solid lubricants (optional) in a resin matrix. Non-metallic, high load, high impact and self lubricating laminated material. Laminated.. |
|||
Shear Strength | 82.7 MPa @Thickness 15.7 mm |
12000 psi @Thickness 0.620 in |
ASTM D732 |
Industrial Laminates/Norplex NP321 Cotton Fabric
(discontinued **) Description: NP321 consists of a fine weave cotton fabric (linen) impregnated with a phenolic resin binder. Applications include vanes for air and liquid pumps, and compressors. NP321 remains very f.. |