Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 13.1 MPa | 1900 psi | Cured 60 minutes at 125°C, Alum/Alum |
Resin Technology Group TIGA 901 Room Temperature Curing Silver Conductive Epoxy 100 parts resin to 6 parts hardener. Cure 24 hours at 25°C, 1-4 hours at 65°C, 30-60 minutes at 125°C, or 30 minutes at 150°C.TIGA 901 is an electrically conductive, silver filled epoxy adhesiv.. |
|||
Shear Strength | 13.1 MPa | 1900 psi | Cured 2 hours at 125°C, Al/Al |
Resin Technology Group TIGA 908 Gold Bonder - Low Stress Silver Conductive 100 parts resin to 6 parts hardener.TIGA 908 is a low stress, conductive silver filled epoxy adhesive. It is recommended for bonding, and sealing electronic applications which require bonding to gol.. |
|||
Shear Strength | 13.1 MPa | 1900 psi | Bond, Al to Al, after 30 days water immersion |
Master Bond EP34AO Epoxy Compound Withstands High Temperatures Description: Master Bond Polymer System EP34AO is a room temperature curing, two component epoxy compound for high temperature bonding and sealing applications especially where thermal conductivity .. |
|||
Shear Strength | 13.1 MPa | 1900 psi | Long Beam Shear, L Direction |
Hexcel® HexWeb® HDC - 3/16 - 16.0 (R2) Heavy Density Core Designation: Material-Cell Size (inches)-DensityHexWeb® HDC is a fabric reinforced honeycomb, typically made from either fiberglass or carbon prepreg. A thermosetting node adhesive is used with eit.. |
|||
Shear Strength | 13.1 MPa | 1900 psi | Overlap, Cold Rolled Steel |
3M Scotch-Weld™ DP125 Gray Epoxy Adhesive Scotch-Weld epoxy adhesive DP125 Gray is a filled, pigmented version of the Scotch-Weld epoxy adhesive DP125 Translucent and has similar performance and flexibility properties.Information provided b.. |
|||
Shear Strength | 13.1 MPa | 1900 psi | Overlap, PVC, Substrate Failure |
3M Scotch-Weld™ DP8005 Black Structural Adhesive 3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8005 is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of polypropyl.. |
|||
Shear Strength | 13.1 MPa | 1900 psi | Overlap, Green FRP, Cohesive Failure |
3M Scotch-Weld™ DP810NS Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 13.1 MPa | 1900 psi | Overlap, PVC, Substrate Failure |
3M Scotch-Weld™ DP8405NS Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP8405NS is a high performance, two-part acrylic adhesives that offer excellent shear, peel and impact performance. These toughened adhesives provide improved adh.. |
|||
Shear Strength | 13.1 MPa @Temperature 66.0 °C |
1900 psi @Temperature 151 °F |
Overlap, Oak, Substrate/Adhesive Failure |
3M Scotch-Weld™ Thick Instant Wood Adhesives and Surface Activator 3M™ Scotch-Weld™ Instant Wood Adhesives an Surface Activator are single component, room temperature-curing adhesives that provides cure and speed and shear strength for demanding applications in t.. |
|||
Shear Strength | 13.1 MPa @Temperature 83.0 °C |
1900 psi @Temperature 181 °F |
Overlap, Etched Alum/Etched Alum |
3M Scotch-Weld™ DP820 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP820 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability .. |
|||
Shear Strength | 13.1 MPa | 1900 psi | Overlap, Stainless Steel/Stainless Steel; ASTM D1002 |
3M Scotch-Weld™ 2216 B/A Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 2216 B/A is a flexible, two-part, room temperature curing epoxy with high peel and shear strength. Scotch-Weld epoxy adhesive 2216 B/A is identical to 3M Scotch-Wel.. |