Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 34.0 - 68.0 MPa | 4930 - 9860 psi | Average value: 55.1 MPa Grade Count:14 |
Overview of materials for Polybutylene Terephthalate (PBT), Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Extrusion Grade". Each property range of values reported is minimum an.. |
|||
Tensile Strength, Ultimate | 34.0 MPa @Temperature 900 °C |
4930 psi @Temperature 1650 °F |
|
Resistalloy International Fecralloy™ 145 Electrical Resistance Steel Ferritic stainless steel with aluminum. Available as wire. Used mainly for electrical elements in both industrial and domestic applications. Industrial applications vary from small laboratory kiln.. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D412 |
Covestro Texin® 5290 Thermoplastic Polyurethane, Polyether-based, Medical
(discontinued **) This grade is in chemical compliance with 21 CFR 177.1680 (Polyurethane Resins) and 177.2600 (Rubber articles intended for repeated use) subject to the limitations of this regulation and any other r.. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D412 |
Covestro Texin® DP7-3008 Thermoplastic Polyurethane, Polyester-based, Aliphatic
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D638 Type IV |
Chevron Phillips Marlex® HHM TR-480Z/M362 Natural high density ethylene hexene copolymer/black concrete
(disc Benefits: good long term hoop strength performance, very high melt strength, outstanding toughness even at low temperatures, concrete base resinCharacteristics: Pipe Ring ESCR > 2000 h, ASTM F 1248;.. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D638 |
Chevron Phillips HiD® 9326 HDPE Natural Pipe Resin
(discontinued **) Resin Type: Linear Copolymer; PE3408 Pipe Resin; ASTM D 3350 Classification: 335440A; ASTM D 4976 Classification: PE 235, A 56606Applications:Base Resin for use in Oil Patch and Industrial Pipe Appl.. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D638 |
Chevron Phillips HiD® 9348 HDPE Natural Pipe Resin
(discontinued **) Resin Type: Linear Copolymer; PE3408 Pipe Resin; ASTM D 3350 Classification: 335440A; ASTM D 4976 Classification: PE 235, A 56606Applications:Base Resin for use in Oil Patch and Industrial Pipe Appl.. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D638 |
ExxonMobil Iotek® 8610 Sodium Ionomer
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A low melt index sodium ionomer made from an ethylene acrylic acid base polymer. It is designed to have high durability, resilience and impact stre.. |
|||
Tensile Strength, Ultimate | 34.0 - 74.0 MPa | 4930 - 10700 psi | Average value: 54.7 MPa Grade Count:3 |
Overview of materials for Phenolic/Rubber; Molded This property data is a summary of similar materials in the MatWeb database for the category "Phenolic/Rubber; Molded". Each property range of values reported is minimum and maximum values of approp.. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | |
Kuraray HYBRAR® PH6 Polypropylene Blend Description: HYBRAR® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRAR® is a special thermoplastic rubb.. |
|||
Tensile Strength, Ultimate | 34.0 MPa @Temperature 1205 °C |
4930 psi @Temperature 2201 °F |
|
Haynes HR-120® alloy, solution heat-treated plate Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | 20 in/min, at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1185 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | 20 in/min, at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1185 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | 20 in/min, at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1185 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D638 |
Total PPH 3281 Polypropylene, Extrusion Grade Low melt flow homopolymer for sheet extrusion, strapping, and in-line thermoforming applicationsMelt Strength – The high melt strength of FINA 3281 allows uniform drawdown during processing, result.. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | 20 in/min, at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1185 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | DIN 53504 |
Lubrizol ESTANE® 5799 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | 5 mm/min |
Arkema Group Rilsan® BMN Y BZ TL Nylon 11, Bronze Bead Filled (Conditioned) Designation ISO 1874-PA11,MHLS,16-020,(Z+M)(B+D)(80BZ+05)Rigid grade with bronze beads (85%) and molybdenum fillers for injection molding. Available color: steel brown. Light and heat stabilized.No .. |
|||
Tensile Strength, Ultimate | 34.0 MPa @Temperature 871 °C |
4930 psi @Temperature 1600 °F |
|
AK Steel 18 SR® Ferritic Stainless steel AK Steel 18 SR® provides excellent resistance to high temperature scaling - far superior to that of Type 446 stainless steel. This material is readily welded by conventional methods. It is not su.. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D412 |
BASF Elastollan® S85A Polyester Type Polyurethane Elastomer Processed by extrusion or injection molding. Elastollan S series of products are polyester-based thermoplastic polyurethanes that exhibit good hydrolytic stability. They also exhibit good oil, fue.. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D638 |
Toyobo E1080A Thermoplastic Polyurethane Elastomer, Extrusion Grade Polybutyleneadipate type, the most general purpose type of Toyobo Polyurethane; features excellent cost-performance. Various grades of Toyobo polyurethane TPEs are used in auto parts, hoses, tubes,.. |
|||
Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D638 |
Toyobo E2080A Thermoplastic Polyurethane Elastomer, Extrusion Grade Polycaprolactone type, featuring a good balance of mechanical strength and chemical resistance. Various grades of Toyobo polyurethane TPEs are used in auto parts, hoses, tubes, sporting goods, shoe.. |
|||
Tensile Strength, Ultimate | 34.0 MPa @Temperature 90.0 °C |
4930 psi @Temperature 194 °F |
ISO 527 |
LATI LARIL 13-V1 Polyphenylene Oxide (PPOm) (UL94V-1)
(discontinued **) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |