Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 17.0 - 32.4 MPa | 2470 - 4700 psi | Average value: 25.1 MPa Grade Count:10 |
Overview of materials for Thermoplastic Olefinic Elastomer (TPO), Blow Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Olefinic Elastomer (TPO), Blow Molding Grade". Each property range of values reported is m.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
ExxonMobil Escorene® LD-701 High EVA Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A fractional melt, 10.5% vinyl acetate copolymer specialty film resin for applications requiring outstanding heat sealability, strength and toughnes.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
ExxonMobil Escorene® LD-705 High EVA Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A fractional melt index, 13.3% vinyl acetate copolymer specialty film resin for applications requiring outstanding heat sealability, strength, and t.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
ExxonMobil Escorene® LD-760 High EVA Compounding Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 27.5% vinyl acetate copolymer designed for specialty compounding applications. Excellent filler acceptance produces highly loaded concentrates.Ap.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
ExxonMobil Escorene® LD-613 EVA Injection Molding Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.An 8.8% vinyl acetate copolymer resin designed for molding and extrusion applications requiring low temperatures, flexibility and toughness. This r.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
Huntsman PE1501 EVA Film Extrusion
(discontinued **) 5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Yields film with excellent impact strength, good heat seal, and good clarity.Applications: Film extrusion: greenhouse film, heavy-duty packa.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
Huntsman PE1503 EVA Film Extrusion
(discontinued **) 5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: Fi.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
Huntsman PE1504 EVA Film Extrusion
(discontinued **) 5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: Fi.. |
|||
Tensile Strength, Ultimate | 17.0 - 216 MPa @Thickness 1.60 - 3.17 mm |
2470 - 31300 psi @Thickness 0.0630 - 0.125 in |
Average value: 86.6 MPa Grade Count:1 |
Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Mineral Filled". Each property range of values reported is minimum and max.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
Solvay Specialty Polymers Algoflon® 25CAR+5CER PTFE; Petroleum Coke and Ceramic Filled
(discontinued **) Data provided by the manufacturer.25 wt.% Petroleum Coke + 5 wt.% Ceramic. Suspension polymer powder grade recommended for compression molding. Pure PTFE possesses high inertness, excellent dielectr.. |
|||
Tensile Strength, Ultimate | 17.0 MPa @Thickness 2.00 mm |
2470 psi @Thickness 0.0787 in |
ASTM D4894 |
3M Dyneon™ TF 4303 PTFE 15% Graphite Filled
(discontinued **) Type II PTFE. Applications include sliding surfaces, bearings, seals/gaskets.Data provided by Dyneon. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | Compounded Tire |
Butyl Rubber (IIR, CIIR, BIIR) Butyl rubber is a copolymer of isoprene (minor) and isobutylene. Chlorobutyl (CIIR) and Bromobutyl (BIIR) contains 1.2% of the halogen. The halogen addition changes the cure characteristics and ca.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | Compounded Tire |
Epichlorohydrin Rubber (CO, ECO) CO is the ISO designation for the homopolymer and ECO is the ISO designation for the ethylene oxide copolymer. Epichlorohydrin rubber is generally damaged by chlorinated solvents, ketones, aldehyde.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D412 |
KKPC KOSYN KTR 301 Thermoplastic Elastomer (TPE) Thermoplastic Elastomer (TPE)Characteristics: KOSYN KTR101 is linear block copolymer made by solution polymerization which polymerizes butadiene and styrene in organic solvent. It is thermoplastics .. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ISO R527-1 |
LyondellBasell Hifaxâ„¢ CA187 Thermoplastic Olefin Resin Key Features: medium melt flow, medium modulus, paintable thermoplastic elastomeric olefin resin, excellent paintability, excellent surface appearance, good impact and stiffness balanceApplications:.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ISO R527-1 |
LyondellBasell Hifaxâ„¢ CB229 Thermoplastic Olefin Resin Key Features: medium high melt flow, medium high modulus, paintable thermoplastic elastomeric olefin resin, excellent impact and stiffness balance, good dimensional stability, excellent processabili.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 395 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 265 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 341 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 341 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 395 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 341 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 395 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638/D412 |
Covestro Baydur® SFR-243 Polyurethane Composite RRIM Foam, 15% Milled Glass Filled, MDI-based 2-Component Liquid System 0.25 in. thickness.Information provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – C.. |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
ExxonMobil Escorene® LD-712 High EVA Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A fractional melt, 10% vinyl acetate copolymer specialty film resin for applications requiring outstanding heat sealability, strength and toughness... |
|||
Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
LyondellBasell Astryn 73A6-3 Polypropylene Copolymer, 30% Calcium Carbonate Key Features: medium high melt flow, medium modulus, mineral-filled polypropylene copolymer, excellent impact and stiffness balance, excellent chemical resistance, excellent aesthetics, high gloss, .. |
|||
Tensile Strength, Ultimate | 17.0 - 303 MPa | 2470 - 43900 psi | Average value: 115 MPa Grade Count:6 |
Overview of materials for Thermoset Polyurethane Foam, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane Foam, Glass Filled". Each property range of values reported is minimum and maximu.. |