Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 118 MPa | 17100 psi | DIN 53455; ASTM D638 |
Kolon KOPA® KN132G15VO G/F Reinforced Flame Retardant Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Tensile Strength, Ultimate | 118 MPa | 17100 psi | DIN 53455; ASTM D638 |
Kolon KOPA® KN135HB30HI Multi Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Tensile Strength, Ultimate | 118 MPa | 17100 psi | |
Shinil Chemical SHINFLAME PC/PBT GF Flame Retardant Polymer Appliance SHINFLAME is a flame retardant (FR) compound which exhibits inherent flame retardant properties during fire. Shinil uses its patented dispersion blending technology with variety of polymers to prod.. |
|||
Tensile Strength, Ultimate | 118 MPa | 17100 psi | ISO 527-1, 2 |
Polyplastics Duranex® 531HS Polybutylene Terephthalate (PBT), Hydrolysis resistant, Heat shock resistant, Heat Shock Resistant DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 118 MPa | 17100 psi | ASTM D638 |
Toyobo Vylopet® EMC430 PET/PBT Blend Key Feature: HB UL-94 ClassApplications: general and high rigidity componentsPET/PBT blends suggested for glossy surfaces. General features of Vylopet® include heat resistance, good mechanical pro.. |
|||
Tensile Strength, Ultimate | 118 MPa | 17100 psi | dry; ISO 527-1/-2 |
DSM Novamid® 1010GN2-15Z BK701 PA6-GF15 FR(17) 15% Glass Reinforced, Flame Retardant, Easy Molding Grade, Injection Molding, High Flow |
|||
Tensile Strength, Ultimate | 118 MPa | 17100 psi | cond; ISO 527-1/-2 |
DSM Novamid® 1015G33-8 NAT PA6-GF33 33% Glass Reinforced, Injection Molding |
|||
Tensile Strength, Ultimate | 118 MPa | 17100 psi | 5mm/min; ISO 527 |
BASF Ultramid® 8231G HS BK-106 14% Glass Filled PA6 (Dry) Ultramid 8231G HS BK-106 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffnes.. |
|||
Tensile Strength, Ultimate | 118 MPa | 17100 psi | 5mm/min; ISO 527 |
BASF Ultramid® 8267G HS BK-106A 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid 8267G HS BK-106A is a heat stabilized, weather resistant, 40% mineral and glass fiber reinforced PA6 injection molding compound with improved UV resistance and sink mark resistance. The co.. |
|||
Tensile Strength, Ultimate | 118 MPa | 17100 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 432 Glass Reinforced, PBT Alloy Data provided by the manufacturer, ComAlloy International Company.33% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 118 MPa @Temperature 60.0 °C |
17100 psi @Temperature 140 °F |
ISO 527 |
LATI LARTON G/30 30% Glass Fiber Filled Polyphenylene sulfide (PPS)
(discontinued **) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex.. |
|||
Tensile Strength, Ultimate | 118 MPa | 17100 psi | DIN 53455; ASTM D638 |
Kolon KOPA® KN135G33HI Multi Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubric.. |
|||
Tensile Strength, Ultimate | 118 MPa @Temperature 90.0 °C |
17100 psi @Temperature 194 °F |
ISO 527 |
LATI LARTON G/40 40% Glass Fiber Filled Polyphenylene sulfide (PPS)
(Unverified Data**) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex.. |