Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 7318 GREY The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
Resinlab® EP1112 Clear Electronic Grade Epoxy Encapsulant Resinlab™ EP 1112 Clear is a two part unfilled fast curing electronic grade epoxy encapsulant designed for small to medium sized castings. It cures completely at room temperature to a tough, flexib.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | post cured- 2 hours at 177°C |
Multibase SILASTIC® C7-4565 TBPB Dow-Corning Biomedical Grade ETR Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | silicone property; ASTM D412 |
Arlon A3020-B004-12 Silicone Rubber/Fiberglass Laminate
(discontinued **) Side 1: cured fusible silicone rubber; Substrate: 25% sinusoidal fiberglass; Side 2: cured fusible silicone rubber; Interleave: 1 mil PE film |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | silicone property; ASTM D412 |
Arlon A3020-T002-12 Silicone Rubber/Fiberglass Laminate
(discontinued **) Side 1: cured fusible silicone rubber; Substrate: 25% sinusoidal fiberglass; Side 2: cured fusible silicone rubber; Interleave: 1 mil PE film |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | silicone property; ASTM D412 |
Arlon A3020-T004-12 Silicone Rubber/Fiberglass Laminate
(discontinued **) Side 1: cured fusible silicone rubber; Substrate: 25% sinusoidal fiberglass; Side 2: cured fusible silicone rubber; Interleave: 1 mil PE film |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | post cured- 8 hours at 177°C; ASTM D412 |
Multibase C6-235 DI-CUP R Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | molded-without post cure; ASTM D412 |
Multibase C6-250 DI-CUP R Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | post cured- 4 hours at 177°C; ASTM D412 |
Multibase C6-250 DI-CUP R Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | molded-without post cure; ASTM D412 |
Multibase C6-250 PERKADOX PD-50S Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | post cured- 8 hours at 177°C; ASTM D412 |
Multibase C6-265 DI-CUP R Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | post cured- 2 hours at 177°C; ASTM D412 |
Multibase C6-265 PERKADOX PD-50S Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | post cured- 4 hours at 177°C; ASTM D412 |
Multibase C6-515 Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
Sylvin Technologies 8950-60 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | |
Sylvin Technologies 9950-60 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 8.30 MPa @Temperature 49.0 °C |
1200 psi @Temperature 120 °F |
Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 460 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 8.30 MPa @Temperature 49.0 °C |
1200 psi @Temperature 120 °F |
Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 660 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | ASTM D638/D412 |
Covestro Baydur® 646 Polyurethane Structural Foam RIM, Density 25 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of.. |
|||
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | |
Dow LDPE 959I Low Density Polyethylene DOW LDPE 959I resin is a medium molecular weight distribution homo polymer designed to offer excellent clarity and flexibility with low warpage for lids. This resin has good processability over a wi.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | ASTM D638 |
Colorite Polymers 87-638A General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | Silicone Rubber Insulator; ASTM D42-68 |
3M 4605 Silicone Rubber Termination Kit 3M™ 4604 and 4605 Quick Term II Silicone Rubber Termination Kits are three-piece Cold Shrink terminations for Tape Shield, Wire Shield, and LC Shield power cables. They meet the requirements of IEE.. |
|||
Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | ASTM D638 |
Buckeye Polymers BP Flex A9008 TPO TPO's are a family of thermoplastic elastomers which exhibit rubber-like properties and are processable on conventional thermoplastic equipment. These resins have excellent UV resistance and have a.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | Silicone Rubber Insulator; ASTM D42 |
3M 5360K Silicone Rubber Termination Kits 3M™ 5630K and 5690K Series Quick Term II Silicone Rubber Termination Kits are one-piece Cold Shrink™ terminations for Tape Shield, Wire Shield and UniShield® power cables. They meet the requireme.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | Silicone Rubber Insulator; ASTM D42 |
3M 5640 Silicone Rubber Termination Kits 3M™ 5640 and 5650 Series Quick Term II Silicone Rubber Termination Kits are one-piece Cold Shrink™ terminations for Jacketed Concentric Neutral (JCN) power cable. They meet the requirements of IEE.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | Silicone Rubber Insulator; ASTM D42 |
3M 5650 Silicone Rubber Termination Kits 3M™ 5640 and 5650 Series Quick Term II Silicone Rubber Termination Kits are one-piece Cold Shrink™ terminations for Jacketed Concentric Neutral (JCN) power cable. They meet the requirements of IEE.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | Silicone Rubber Insulator; ASTM D42-68 |
3M 5680 Cold Shrink Silicone Rubber Termination Kits QT-III 3M™ Cold Shrink 5600 and 5680 Series QT-II Termination Kits contain one-piece silicone rubber terminations designed for concentric neutral (CN) cable. They meet the requirements of IEEE 48-1990 for.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | ASTM D412; ISO 37 |
Advanced Polymer Alloys Alcryn® 3055 NC Melt Processable Rubber Alcryn melt-processable rubber (MPR) is a true rubber, based on a partially cross-linked, chlorinated olefin interpolymer alloy. Alcryn is designed for the manufacture of rubber parts with high prod.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | ASTM D638 |
Colorite Polymers 5002 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 8.27 MPa | 1200 psi | ASTM D412 |
G-2703 Styrene-based Biomedical Elastomer |