Polymer Property : Tensile Strength, Ultimate = 117000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	805 MPa	117000 psi	Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
Outokumpu 4501 Duplex Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto) form.
Tensile Strength, Ultimate	807 MPa	117000 psi	RT, Dry, 90° Direction
Renegade Materials Corporation MVK-14 Polyimide FreeForm™ S2-Glass Fabric MVK-14 Polyimide Astroquartz and S2 glass prepregs are an affordable, easy-to-process material for high-temperature radome and antenna applications. MVK-14 is a non-MDA alternative to BMI, cyanate e..
Tensile Strength, Ultimate	805 MPa	117000 psi
Haynes HastelloyÂ® N, weld metal, aged 500 hours at 649Â°C (1200Â°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870Â°C (1300-1600Â°F), good oxidation resistance in air.Data provided by the man..
Tensile Strength, Ultimate	805 MPa	117000 psi
Haynes HastelloyÂ® W alloy as a weld filler, base metal Alloy 188/ Multimet alloy 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica..
Tensile Strength, Ultimate	809 MPa	117000 psi
Haynes HR-160Â® alloy, plate, aged 4000 hours at 760Â°C (1400Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Tensile Strength, Ultimate	805 MPa	117000 psi
Haynes 556Â® alloy, 0% cold reduction, 1121Â°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	810 MPa	117000 psi
Haynes 556Â® alloy, 10% cold reduction, 1121Â°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	805 MPa	117000 psi
Haynes 556Â® alloy, hot rolled, solution annealed plate, 6.4-12.7 mm (1/2 in.) thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	807 MPa	117000 psi
Universal Wire Works 617 Nickel Alloy Welding Wire Alloy 617 is used for TIG and MIG welding of Inconel type alloy 617 and alloys of similar composition. Alloy 617 welds produce high stress-rupture strength in prolonged exposure to high temperatures..
Tensile Strength, Ultimate	805 MPa @Temperature 705 °C	117000 psi @Temperature 1300 °F
Haynes 242® alloy, hot rolled plate, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good thermal..