Universal Wire Works 617 Nickel Alloy Welding Wire

Category	Metal , Nonferrous Metal , Nickel Alloy
Manufacturer	Universal Wire Works
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Universal Wire Works 617 Nickel Alloy Welding Wire.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Alloy 617 is used for TIG and MIG welding of Inconel type alloy 617 and alloys of similar composition. Alloy 617 welds produce high stress-rupture strength in prolonged exposure to high temperatures. Alloy 617 is best used on applications subjected to elevated temperatures about 1400 degrees. Alloy 617 is excellent for welding alloys 600, 601, 800h, 800HT and 803, and for cast alloys HK-40, HP and HP-45 MOD.Information provided by Universal Wire Works for their line of welding wire and filler metal.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	807 MPa	117000 psi
	296 MPa @Temperature 871 °C	43000 psi @Temperature 1600 °F
Tensile Strength, Yield	503 MPa	73000 psi
	262 MPa @Temperature 871 °C	38000 psi @Temperature 1600 °F
Elongation at Break	41 %	41 %
	33 % @Temperature 871 °C	33 % @Temperature 1600 °F

Component Elements Properties	Metric	English	Comments
Aluminum, Al	1.2 %	1.2 %
Carbon, C	0.070 %	0.070 %
Chromium, Cr	22 %	22 %
Cobalt, Co	12.5 %	12.5 %
Copper, Cu	0.20 %	0.20 %
Iron, Fe	1.5 %	1.5 %
Manganese, Mn	0.50 %	0.50 %
Molybdenum, Mo	9.0 %	9.0 %
Nickel, Ni	52.3 %	52.3 %	As Remainder
Phosphorous, P	0.0080 %	0.0080 %
Silicon, Si	0.50 %	0.50 %
Sulfur, S	0.0060 %	0.0060 %
Titanium, Ti	0.20 %	0.20 %