Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 34.5 - 300 MPa | 5000 - 43500 psi | Average value: 118 MPa Grade Count:164 |
Overview of materials for Nylon 66, Heat Stabilized This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Heat Stabilized". Each property range of values reported is minimum and maximum values of appr.. |
|||
Tensile Strength, Ultimate | 137 - 300 MPa | 19900 - 43500 psi | Average value: 217 MPa Grade Count:30 |
Overview of materials for Nylon 66, 30% Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Carbon Fiber Filled". Specific grades with carbon fiber content between 25% and 34% are in.. |
|||
Tensile Strength, Ultimate | 270 - 300 MPa | 39200 - 43500 psi | |
CLAL-MSX SICLANIC S® TB Quenched Copper Alloy SICLANIC S® is particularly recommended for the production of conductive contact blades. SICLANIC S® offers :electrical conductivity greatly superior to that of bronzes, brasses and nickel silver.. |
|||
Tensile Strength, Ultimate | 80.0 - 300 MPa | 11600 - 43500 psi | |
Alliance A-5S Alnico Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 - 300 MPa | 11600 - 43500 psi | |
Alliance A-8S Alnico Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 - 300 MPa | 11600 - 43500 psi | |
Alliance A-6S Alnico Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 - 300 MPa | 11600 - 43500 psi | |
Alliance A-2S Alnico Magnetic Material |
|||
Tensile Strength, Ultimate | 10.3 - 300 MPa | 1500 - 43500 psi | Average value: 31.7 MPa Grade Count:167 |
Overview of materials for Polypropylene, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Flame Retardant". Each property range of values reported is minimum and maximum values of.. |
|||
Tensile Strength, Ultimate | 13.8 - 300 MPa | 2000 - 43500 psi | Average value: 89.6 MPa Grade Count:23 |
Overview of materials for Epoxy Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Epoxy Molding Compound". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Tensile Strength, Ultimate | 100 - 300 MPa | 14500 - 43500 psi | Average value: 208 MPa Grade Count:29 |
Overview of materials for Polyphthalamide (PPA), Carbon Fiber + PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Carbon Fiber + PTFE Filled". Each property range of values reported is minimum and maxi.. |