Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ASTM D638 |
NCMT NanoPAC™ G3000 High Performance Polypropylene Nanocomposite Applications: Automobile Construction MaterialInformation provided by Nano Composite Materials Technology Limited |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ISO 527 |
LATI LAPEX A Polyethersulfone (PES) (UL94 V-0)
(Unverified Data**) Description: Lapex A compounds are polyethersulfone (PES) products. They are high temperature compounds offering an interesting combination of properties. Lapex A provides outstanding thermal resist.. |
|||
Tensile Strength, Ultimate | 80.0 - 120 MPa | 11600 - 17400 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 8808/0902 Carbon Fiber Reinforced PVDF Compound
(discontinued **) Key features of this grade: Carbon Fiber Reinforcement, Formulated. Recommended processing is injection. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinate.. |
|||
Tensile Strength, Ultimate | 80.0 MPa @Temperature 427 °C |
11600 psi @Temperature 800 °F |
Brass butt joint |
Lucas-Milhaupt SIL-FOS Silver/ Copper/ Phosphorus Alloy Applications: Sil-Fos was developed primarily for use on copper, but their use has extended to other nonferrous copper base alloys. It is used extensively on refrigeration units, air conditioning .. |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ISO 527 |
Solvay Technyl® B 50H1 Nylon 66/6, Flame Retardant, EH0 Flame retardant copolyamide 66/6, unreinforced, heat stabilized, for injection molding.This phosphorus and halogen free flame retardant grade, UL 94 VO (0.4 mm), offers excellent filling qualities a.. |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ISO 527 |
Sumitomo Bakelite North America RX® 611 Fiberglass Reinforced Phenolic RX 611 is a fiberglass reinforced phenolic molding compound, with good dimensional stability and good strength at elevated temperatures. Meets ASTM D-5948 Type MFH.Information supplied by Sumitomo.. |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ASTM D638 |
Tipco Tipcolene® SEB 200 - 20% Chemically Coupled Glass Fiber Polypropylene Homopolymer with High Heat Stability 20% Chemically Coupled Glass Reinforced PP HomopolymerApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ISO 527 |
Wellman Wellamid® 220-N Unfilled Nylon 66, Not Lubricated, Nucleated, or Heat Stabilized Typical Applications: Automotive components, gears, switches, bearings, pulleys, fasteners, electrical coil forms, chain-saw hand guards, cable ties, furniture hardware, small appliance housings, ae.. |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ISO 527 |
Wellman Wellamid® MR410 42H-N 40% Mineral Reinforced Nylon 6, Heat Stabilized Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive co.. |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | dry; ISO 527-1/-2 |
DSM Stanyl® TS272A1 PA46-RF Aramid fiber reinforced, Wear and Friction Modified |
|||
Tensile Strength, Ultimate | 80.0 - 94.0 MPa | 11600 - 13600 psi | |
Dow CYCLOTENE™ 3022-35 Bisbenzocyclobutene (BCB) Electronic Resin This product was developed for use as spin-on dieletric materials in microelectronic fabrication.Information provided by Dow |
|||
Tensile Strength, Ultimate | 80.0 - 94.0 MPa | 11600 - 13600 psi | |
Dow CYCLOTENE™ 3022-63 Bisbenzocyclobutene (BCB) Electronic Resin This product was developed for use as spin-on dieletric materials in microelectronic fabrication.Information provided by Dow |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | 5 mm/min |
Arkema Group Orgalloy® RS 6010 Nylon 6 Alloy, 10% Glass Fiber Reinforced (Conditioned) RS 60 series, rigid polyamide 6 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties.. |
|||
Tensile Strength, Ultimate | 80.0 - 300 MPa | 11600 - 43500 psi | |
Alliance A-5S Alnico Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-28UH Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-30EH Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-35M Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-35UH Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-38SH Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-42SH Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-44H Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ISO R527 |
Arkema Group Orgalloy® RS 6010 Polyamide 6 Alloy 10% Glass Fiber reinforced Polyamide Alloy, Rigid grade, Nylon 6 basedMolding of Engineering PartsInformation provided by Arkema Group |
|||
Tensile Strength, Ultimate | 80.0 - 300 MPa | 11600 - 43500 psi | |
Alliance A-6S Alnico Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-30EZ Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-33UH Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-38H Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | |
Alliance N-42H Neodymium Iron Boron Magnetic Material |
|||
Tensile Strength, Ultimate | 80.0 - 123 MPa @Temperature 150 - 250 °C |
11600 - 17800 psi @Temperature 302 - 482 °F |
Average value: 97.0 MPa Grade Count:2 |
Overview of materials for Epoxy Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Epoxy Molding Compound". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ASTM D638 |
Sumitomo Bakelite North America FM 4004F Fiberglass and Mineral Reinforced Phenolic Novolac FM 4004F is a fiberglass and mineral reinforced phenolic novolac compound with improved strength properties over FM 4004. This compound exhibits excellent dimensional stability and good strength at.. |
|||
Tensile Strength, Ultimate | 80.0 - 90.0 MPa @Temperature 80.0 - 80.0 °C |
11600 - 13100 psi @Temperature 176 - 176 °F |
Average value: 85.3 MPa Grade Count:4 |
Overview of materials for Polypropylene with 60% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 60% Glass Fiber Filler". Specific grades with glass content between 55% and 64% are i.. |