Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | >= 310 MPa | >= 45000 psi | |
MetalTek C81500 Chrome Copper High Conductivity Information provided by MetalTekCast UNS C81500; Cast Grade C81500; Military MIL-C-19310 |
|||
Tensile Strength, Ultimate | >= 310 MPa | >= 45000 psi | |
MetalTek MTEK 102-N Cast UNS C92900 Gear Bronze Copper-tin alloy with high tensile, yield and compressive strength as well as wear resistance.Applications: Worm gears, steel mill nutsInformation provided by MetalTekCast UNS C92900; Cast Grade C92.. |
|||
Tensile Strength, Ultimate | >= 310 MPa | >= 45000 psi | |
MetalTek MTEK 90-10 UNS C96200 Nickel-Copper Alloy Information provided by MetalTek |
|||
Tensile Strength, Ultimate | 310 MPa @Temperature 23.0 °C |
45000 psi @Temperature 73.4 °F |
|
Lucas-Milhaupt EASY FLO Silver Based Cadmium-Bearing Filler Metal Applications: Easy-Flo is very versatile and can be used successfully on nearly all nickel, iron and copper base alloys. In certain instances, special fluxes, may be required to obtain good wettin.. |
|||
Tensile Strength, Ultimate | 310 MPa @Temperature 870 °C |
45000 psi @Temperature 1600 °F |
|
Haynes Hastelloy® W alloy, gas metal arc welds, as-welded Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
Tensile Strength, Ultimate | 310 MPa @Temperature 870 °C |
45000 psi @Temperature 1600 °F |
|
Haynes Hastelloy® X alloy, sheet Solid-solution-strengthened with very good high-temperature strength and very good resistance to oxidizing environments up to about 1095°C, and good carburization resistance. Applications includ.. |
|||
Tensile Strength, Ultimate | >= 310 MPa | >= 45000 psi | |
MetalTek MTEK 65+Ni UNS C91600 Gear Bronze Copper-tin alloy with high tensile, yield and compressive strength as well as wear resistance.Applications: Worm gears, steel mill nutsInformation provided by MetalTekCast UNS C91600; Cast Grade C91.. |
|||
Tensile Strength, Ultimate | 310 - 379 MPa @Temperature 20.0 °C |
45000 - 55000 psi @Temperature 68.0 °F |
|
H.C. Starck Ultra 76 Alloy (Ta 2.5%W) Benefits: Significantly improved corrosion resistance in HCl and H2SO4 acids.Minimized hydrogen embrittlement rates compared to standard NRC®76Up to 100 times lower in HCl acidUp to 10 times low.. |
|||
Tensile Strength, Ultimate | >= 310 MPa | >= 45000 psi | |
Alcoa Toolrite 2011®-T3 Aluminum Weldability = D; Stress Corrosion Cracking Resistance = D; General Corrosion Resistance = D (A = best; E = worst). General 2011 characteristics and uses: Good machinability, especially free-cutting .. |
|||
Tensile Strength, Ultimate | 310 - 421 MPa | 45000 - 61000 psi | |
Eagle Brass 260 Cartridge Brass, Annealed Alloy C260 is commonly used for electrical components, electronic parts, and mechanical fasteners. The alloy has good strength but poor stress relaxation characteristics and does not make a particul.. |
|||
Tensile Strength, Ultimate | 310 - 407 MPa | 45000 - 59000 psi | |
Eagle Brass 425 Tin Brass 2%, 1/4 Hard Alloy C425 is a low zinc-containing alloy with good combination of tensile strength, electrical conductivity, formability and corrosion resistance. Applications include electrical springs, connector.. |
|||
Tensile Strength, Ultimate | 310 - 448 MPa | 45000 - 65000 psi | |
Eagle Brass 725 Copper Nickel Tin, Annealed Alloy C725 is a moderate strength, low conductivity alloy with excellent bare solderability and corrosion resistance. Applications include electronic parts, springs, connectors and wire wrap termina.. |
|||
Tensile Strength, Ultimate | 310 MPa @Temperature 538 °C |
45000 psi @Temperature 1000 °F |
|
Crucible Steel 416 Plus Chromium Steel Crucible 416 Plus is a hardenable chromium steel to which elements have been added to improve machinability and non-galling characteristics. Better machinability than that of standard AISI Type 4.. |
|||
Tensile Strength, Ultimate | 310 MPa | 45000 psi | Calculated from tenacity |
DuPont™ Nomex® 455 (NOMEX III) Aramid Staple Fiber Type 455 staple of NOMEX, a patented blend of NOMEX and KEVLAR brand fibers, was introduced to fill the need for higher performance thermal protective apparel. Type 450 staple. However, because of.. |
|||
Tensile Strength, Ultimate | 310 MPa | 45000 psi | Calculated from tenacity |
DuPont™ Nomex® 462 (NOMEX IIIA) Aramid Staple Fiber Type 462 staple of NOMEX is a blend of NOMEX and KEVLAR brand fibers and P-140, a proprietary static dissipative fiber. When converted to fabric it is known commercially as NOMEX IIIA and is used f.. |
|||
Tensile Strength, Ultimate | 310 MPa | 45000 psi | annealed |
CMW® ELKONIUM 1 silver, copper, nickel alloy Alloying copper into silver increases the hardness of the material, and its resistance to mechanical wear and deformation. The electrical and thermal conductivity remain relatively high, thus, the a.. |
|||
Tensile Strength, Ultimate | 310 MPa @Temperature 760 °C |
45000 psi @Temperature 1400 °F |
|
Carpenter 20Cb-3® Stainless Steel Data provided by Carpenter Technology Corporation.20Cb-3® is an austenitic stainless steel possessing excellent resistance to hot sulfuric acid and many other aggressive environments which would re.. |
|||
Tensile Strength, Ultimate | >= 310 MPa | >= 45000 psi | |
AK Steel Cold Rolled Carbon Steel, Dent Resistant (DR 180), SAE J2340 Type 180 A Information provided by AK Steel |
|||
Tensile Strength, Ultimate | >= 310 MPa | >= 45000 psi | |
AK Steel Grade 30 Cold Rolled Carbon Steel, Structural Steel (SS) Information provided by AK Steel |
|||
Tensile Strength, Ultimate | 310 MPa | 45000 psi | .0275 - .035 inches sheet thickness; ASTM A 370 |
AK Steel ZINCGRIP® GA Hot Dip Galvannealed Carbon Extra Deep Drawing Steel (EDDS), Standard Grade Interstitial Free (I-F) steels are made by adding titanium and/or columbium to the molten steel after degassing and offer excellent drawability.Information provided by AK Steel |
|||
Tensile Strength, Ultimate | 310 MPa | 45000 psi | .0275 - .035 inches sheet thickness; ASTM A 370 |
AK Steel ZINCGRIP® Hot Dip Galvanized Carbon Steel, Extra Deep Drawing Steel (EDDS), Standard Grade Interstitial Free (I-F®) steels are made by adding titanium and/or columbium to the molten steel after vacuum degassing and offer excellent drawability.Information provided by AK Steel |
|||
Tensile Strength, Ultimate | 310 MPa | 45000 psi | |
AK Steel Aluminized Carbon Steel, Extra Deep Drawing Steel (EDDS), Standard Grade Aluminized Type 1 coating contains approximately 91% aluminum and 9% silicon that is metallurgically bonded to the low-carbon steel substrate. Interstitial Free (I-F) steels are made by adding tita.. |
|||
Tensile Strength, Ultimate | 310 MPa | 45000 psi | |
AK Steel Aluminized Carbon Steel, Extra Deep Drawing Steel Plus (EDDS+), Standard Grade Aluminized Type 1 coating contains approximately 91% aluminum and 9% silicon that is metallurgically bonded to the low-carbon steel substrate. Interstitial Free (I-F) steels are made by adding tita.. |
|||
Tensile Strength, Ultimate | >= 310 MPa | >= 45000 psi | |
AK Steel ZINCGRIP® 230, Grade 33 Hot Dip Galvanized Carbon Steel, Structural Steel (SS) Information provided by AK Steel |
|||
Tensile Strength, Ultimate | 310 MPa | 45000 psi | .0275 - .035 inches sheet thickness; ASTM A 370 |
AK Steel ZINCGRIP® ELECTRASMOOTH® Electrogalvanized Carbon Steel, Extra Deep Drawing Steel Plus (EDDS+), Standard Grade Interstitial Free (I-F) steels are made by adding titanium to the molten steel after degassing and offer excellent drawability.Information provided by AK Steel |
|||
Tensile Strength, Ultimate | >= 310 MPa | >= 45000 psi | |
AK Steel ZINCGRIP® Hot Dip Galvanized Carbon Steel, AASHTO M218, CSP Information provided by AK Steel |
|||
Tensile Strength, Ultimate | >= 310 MPa | >= 45000 psi | Minimum |
Aleris Weldural Aluminum Alloy, 500 mm Thickness Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldab.. |
|||
Tensile Strength, Ultimate | 310 MPa | 45000 psi | |
Ametek 17-4 P/M Process, Sintered at 2050°F (1121°C) Composition reported is typical of 17-4 precipitation hardening stainless. This alloy is widely used because of its high strength, high hardness, excellent corrosion resistance, and easy heat treat.. |
|||
Tensile Strength, Ultimate | 310 MPa @Temperature 871 °C |
45000 psi @Temperature 1600 °F |
|
Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |