Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D638 |
Rostone Rosite® 3552C BMC Thermoset Polyester, 15% Glass Reinforced
(discontinued **) Key Features: High Stability, Non-OutgassingDesigned for applications requiring excellent stability and dimensional control. Out-gassing is virtually eliminated making it ideal for systems such as .. |
|||
Tensile Strength, Ultimate | 27.6 - 186 MPa | 4000 - 27000 psi | Average value: 139 MPa Grade Count:22 |
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler". Specific grades with carbon fiber content bet.. |
|||
Tensile Strength, Ultimate | >= 27.6 MPa | >= 4000 psi | Reinforced |
Natural Rubber, Not Vulcanized (NR, IR, Polyisoprene) Natural rubber is polyisoprene. Chemical and environmental resistance and mechanical properties are improved through crosslinking (vulcanizing), usually through treatment with sulfur.Natural rubber.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | 2 in/min.; ASTM D638 |
Ineos K44-06-122 HDPE HDPE K44-06-122 is a natural high density polyethylene copolymer designed specifically for extrusion of potable water, industrial, and mining pipe. It is recognized by the Plastic Pipe Institute as .. |
|||
Tensile Strength, Ultimate | >= 27.6 MPa | >= 4000 psi | ISO 1184-1983E |
LyondellBasell DP 0110M Polybutene Key Features: highly isotactic, semi-crystalline nucleated homopolymer, good creep resistance, good environmental stress crack resistance, FDA acceptable, easily dispersibleApplications: packaging i.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | Machine direction |
Spartech Royalstatâ„¢ R671 ABS Static Control Sheet Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | |
Williams Advanced Alloys WS314A Solder All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D412/D638 |
Lubrizol Estane® MVT 80AF3 Thermoplastic Polyurethane, Moisture Vapor Transmission Type: Estane® MVT 80AF3 TPU is a aromatic polyether-based thermoplastic polyurethane (TPU).Features: High moisture vapor transmission, good low temperature properties and elasticity.Uses: Blown and.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D638 |
Eastman Tenite Propionate 307A2R30018 Natural, Trsp Cellulose Acetate Propionate Plasticizer 18%. Weight loss on heating = 1% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pro.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D638 |
Buckeye Polymers BP RPPC 0510 Blk Reprocessed Polypropylene, Unfilled This reprocessed product is successful in applications where cost is a major specification, yet physical characteristics require product performance. Industrial recycled resin compounds are utilize.. |
|||
Tensile Strength, Ultimate | 27.6 - 41.4 MPa | 4000 - 6000 psi | |
Bulk Molding Compounds BMC 100 Thermoset Polyester, GP BMC 100 is a high strength, low shrink general purpose molding compound. It can be supplied in bulk or extruded in pre-weighted slugs. Due to the excellent flow and controlled reactivity, BMC 100 is.. |
|||
Tensile Strength, Ultimate | 27.6 - 41.4 MPa | 4000 - 6000 psi | |
Bulk Molding Compounds BMC 604 Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 604 molding compound is a low-cost, mineral filled glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is a general purpose material wit.. |
|||
Tensile Strength, Ultimate | 27.6 - 48.3 MPa | 4000 - 7000 psi | |
Bulk Molding Compounds BMC 605LWR Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 605LWR is a mineral filled, glass fiber reinforced polyester bulk molding compound suitable for compression, transfer and stuffer injection molding. It is designed to provide improved wear resis.. |
|||
Tensile Strength, Ultimate | 27.6 - 34.5 MPa | 4000 - 5000 psi | |
Bulk Molding Compounds BMC 902 Thermoset Polyester, Soft Flow Encapsulation Grade BMC 902 is a medium strength, high flow molding compound that meets Ford Specification ESFM3D114- A. BMC 902 has excellent electrical properties and creep resistance. It can be pigmented in a wide r.. |
|||
Tensile Strength, Ultimate | 27.6 - 48.3 MPa | 4000 - 7000 psi | |
Bulk Molding Compounds BMC 1100 Corelyn Glass Fiber Reinforced Polyester Compound BMC 1100, also known as CoreLyn, is a food contact safe material with excellent scratch and stain resistant properties. CoreLyn can be pigmented to match virtually any color. This glass fiber-reinfo.. |
|||
Tensile Strength, Ultimate | 27.6 - 41.4 MPa | 4000 - 6000 psi | |
Bulk Molding Compounds BMC 200 Thermoset Polyester, Electrical Grade BMC 200 is a high strength, low shrink molding compound. It can be supplied in bulk or extruded in pre-weighted slugs.Typical applications are circuit breakers, insulators, bobbins, electrical conne.. |
|||
Tensile Strength, Ultimate | 27.6 - 55.2 MPa | 4000 - 8000 psi | |
Bulk Molding Compounds BMC 324 Automotive Grade Molding Compound BMC 324 is a low profile, automotive grade molding compound that is suitable for Injection, Compression or Transfer molding operations. BMC 324 can be metallized directly, without an initial base-co.. |
|||
Tensile Strength, Ultimate | 27.6 - 124 MPa | 4000 - 18000 psi | Average value: 83.6 MPa Grade Count:99 |
Overview of materials for Polycarbonate, Glass + PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Glass + PTFE Filled". Each property range of values reported is minimum and maximum value.. |
|||
Tensile Strength, Ultimate | 27.6 - 31.0 MPa | 4000 - 4500 psi | TM R050-36 |
Resinlab® EP1195 Flame Retardant Epoxy Casting Resin Resinlab™ EP1195 is a low viscosity, fast gelling, flame retardant epoxy casting resin system. It is recognized under the Component Recognition Program of Underwriters Laboratories Inc., (File # E1.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | TM R050-36 |
Resinlab® EP1300 Black Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP1300 Black (Formerly Lab Product W092602) is a two part unfilled electronic grade epoxy encapsulant designed for small to medium sized castings. It has a pot life of about one hour and .. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | TM R050-36 |
Resinlab® EP1300 Clear Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP1300 Clear (Formerly Lab Product W092602) is a two part unfilled electronic grade epoxy encapsulant designed for small to medium sized castings. It has a pot life of about one hour and .. |
|||
Tensile Strength, Ultimate | <= 27.6 MPa | <= 4000 psi | With carbon black or gum stocks. ASTM D412-80 |
DuPont Performance Polymers Hypalon® 40S Chlorosulfonated Polyethylene Rubber, General Description
(discontin Product form is white, odorless chips. Distinguishing Feature: Low viscosity polymer. Improves processing of dry stiff stocks.35 % Chlorine Content. 1% Sulfur Content. Excellent Abrasion Resista.. |
|||
Tensile Strength, Ultimate | <= 27.6 MPa | <= 4000 psi | With carbon black or gum stocks. ASTM D412-80 |
DuPont Performance Polymers Hypalon® 40 Chlorosulfonated Polyethylene Rubber, General Description
(discontinu Product form is white, odorless chips. Distinguishing Feature: Medium polymer viscosity. Versatile.35 % Chlorine Content. 1% Sulfur Content. Excellent Abrasion Resistance. Excellent Chemical Re.. |
|||
Tensile Strength, Ultimate | <= 27.6 MPa | <= 4000 psi | With carbon black or gum stocks. ASTM D412-80 |
DuPont Performance Polymers Hypalon® 4085 Chlorosulfonated Polyethylene Rubber, General Description
(disconti Product form is white, odorless chips. Distinguishing Feature: High polymer viscosity. Good green strength. Improves processing of soft or highly extended stocks.36 % Chlorine Content. 1% Sulfur.. |
|||
Tensile Strength, Ultimate | <= 27.6 MPa | <= 4000 psi | With carbon black or gum stocks. ASTM D412-80 |
DuPont Performance Polymers Hypalon® 48 Chlorosulfonated Polyethylene Rubber, General Description
(discontinu Product form is white, odorless chips. Distinguishing Feature: High polymer viscosity. Excellent oil and fluids resistance. High uncured strength.43 % Chlorine Content. 1% Sulfur Content. Excel.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | |
Sylvin Technologies 9604-95C Clear PVC for Injection Molding Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | TM R050-36 |
Resinlab® EP1046FG Clear Electronic Grade Epoxy Encapsulant Resinlab™ EP1046FG Clear is a two part unfilled very fast curing electronic grade epoxy encapsulant designed for small castings (less than 25 grams). It cures very quickly with low exotherm to a to.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | TM R050-36 |
Resinlab® EP1190 Flame Retardant Epoxy Casting Resin Resinlab™ EP1190 is a medium viscosity, flame retardant epoxy casting resin system. It is recognized under the Component Recognition Program of Underwriters Laboratories Inc., (File# E186034, Proje.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D638 |
Buckeye Polymers BP RPP 2007 TR Blk Reprocessed Polypropylene, 20% Mineral Filled Talc Filled BlackThis reprocessed product is successful in applications where cost is a major specification, yet physical characteristics require product performance. Industrial recycled resin comp.. |