Polymer Property : Tensile Strength, Ultimate = 22.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	22.0 MPa	3190 psi	ISO 527-1
Polikim ULPOLEN® 1000 UHMWPE, Flame Retardant For those producing flammable materials and in the mining industry, explosion and fire are major dangers. It is of vital importance that in conveyor belts and bunkers, lining material is flame retar..
Tensile Strength, Ultimate	22.0 MPa	3190 psi	ISO 527-1
Polikim ULPOLEN® 1000 UHMWPE, UV, Antistatic In tough operating conditions and under direct sunlight, standard Ulpolen® 1000 shows signs of wear and abrasion within a period shorter than a year. It accumulates static electric during daily use..
Tensile Strength, Ultimate	22.0 MPa	3190 psi	ASTM D638
NCMT NanoPAC™ S201 High Performance Polypropylene Nanocomposite Characteristics: High stiffness Supplementary of ABS Good impact resistant Less shrinkage Good thermal conductivity Applications: Electrical Appliances AutomobileInformation provided by Nano Composi..
Tensile Strength, Ultimate	22.0 MPa	3190 psi	ISO 527
Premix Thermoplastics PRE-ELEC® PS 1328 PRE-ELEC PS 1328 is a conductive thermoplastic compound based on polystyrene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC ..
Tensile Strength, Ultimate	22.0 - 28.0 MPa	3190 - 4060 psi
Solvay Specialty Polymers Hyflon® PFA 450 Fluoropolymer (discontinued **) Data provided by the manufacturer.Hyflon® PFA 450 has outstanding physical and chemical properties typical of fluoropolymers.Hyflon® PFA 420
Tensile Strength, Ultimate	22.0 - 31.0 MPa	3190 - 4500 psi	Average value: 28.3 MPa Grade Count:6
Overview of materials for High Density Polyethylene (HDPE), Carbon Black Filled This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Carbon Black Filled". Each property range of values reported is minimu..
Tensile Strength, Ultimate	22.0 - 39.0 MPa	3190 - 5660 psi	Average value: 31.6 MPa Grade Count:18
Overview of materials for Polyperfluoroalkoxyethylene (PFA), Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyperfluoroalkoxyethylene, Molded/Extruded". Each property range of values reported is minimum and max..
Tensile Strength, Ultimate	22.0 MPa @Temperature 90.0 °C	3190 psi @Temperature 194 °F	ISO 527
LATI LATILUB 82-01M Nylon 12 Base, 1% Molybdenum Disulfide Self Lubricating Plastic (discontinued **) Description: Latilub self-lubricating plastic materials are more and more often designed to replace metals in applications such as gears, bushings, cams, slides, etc), for which, besides their intri..
Tensile Strength, Ultimate	22.0 - 80.0 MPa @Temperature 80.0 - 120 °C	3190 - 11600 psi @Temperature 176 - 248 °F	Average value: 50.9 MPa Grade Count:1
Overview of materials for Nylon 66, Glass/Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass/Mineral Filled". Each property range of values reported is minimum and maximum values of..
Tensile Strength, Ultimate	>= 22.0 MPa	>= 3190 psi	ISO 1184-1983E
LyondellBasell Montell 0800 Polybutene Key Features: highly isotactic, semi-crystalline homopolymer, good creep resistance, good environmental crack resistance, miscible with polypropylenes, FDA acceptableApplications: concrete carrierMe..
Tensile Strength, Ultimate	22.0 MPa	3190 psi	Type 1, 2"/min; ASTM D638
StratasysÂ® ABS ABS is a strong, durable production-grade thermoplastic used across many industries. ABS is an ideal material for conceptual prototyping through design verification through direct digital manufactur..
Tensile Strength, Ultimate	22.0 MPa @Temperature 80.0 °C	3190 psi @Temperature 176 °F	ASTM D638
Toyobo NB-5620S Nylon/Olefin Alloy, 15% Mineral Reinforced (Conditioned) Features: 15% Mineral Reinforced, Light WeightInformation provided by Toyobo.
Tensile Strength, Ultimate	22.0 MPa	3190 psi	at max load; ISO 527
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized..
Tensile Strength, Ultimate	22.0 MPa	3190 psi	at max load; ISO 527
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized..
Tensile Strength, Ultimate	22.0 MPa	3190 psi	at max load; ISO 527
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized..
Tensile Strength, Ultimate	22.0 MPa	3190 psi	ASTM D638/D412
Covestro Baydur® 660 IBS Polyurethane Structural Foam RIM, Density 40 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. IBS = Interactive Blowing System RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience ..
Tensile Strength, Ultimate	22.0 MPa	3190 psi	ASTM D638/D412
Covestro Baydur® STR/F-275 IMR Polyurethane Composite SRIM Foam, 20% Glass Filled, MDI-based 2-Component Liquid System Contains continuous strand fiberglass mat.0.0985 in. thickness.Information provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer..
Tensile Strength, Ultimate	22.0 MPa	3190 psi	ASTM D638/D412
Covestro Bayflex® 110-80 Polyurethane Elastomeric RIM, 15% Milled Glass Reinforced, MDI-based 2-Component Liquid System 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and o..
Tensile Strength, Ultimate	22.0 MPa	3190 psi	ISO 527
DSM Fibre Intermediates Nyrim® 4000 (Conditioned) Conditioned at 23°C and 50% Relative Humidity.Nyrim is a Block Copolymer of Nylon 6 and an elastomer with exceptional properties in impact resistance, fatigue and abrasion resistance. Nyrim is proc..
Tensile Strength, Ultimate	22.0 MPa	3190 psi	Vulcanizate, Press cured, TC95 +3min at 160°C
Dow Nordel® IP 4725P Heat Resistant Molding FormulationNordel® IP 4725P
Tensile Strength, Ultimate	22.0 MPa	3190 psi	Die C (35 min / 145°C); ASTM D412
Dow SE SLR-4400 Solution polymerized Styrene Butadiene Rubber (S-SBR) SE SLR-4400 is manufactured by anionic solution polymerization using lithium initiator. It is a product with medium styrene and high vinyl content. The product is partially Sn-coupled and non-stai..
Tensile Strength, Ultimate	22.0 MPa @Thickness 1.14 - 1.52 mm, Temperature 704 °C	3190 psi @Thickness 0.0449 - 0.0598 in, Temperature 1300 °F
AK Steel 409 Ferritic Stainless steel AK Steel 409 Stainless Steels are especially useful for applications where oxidation or corrosion protection beyond the capacity of carbon steel and some coated steels is needed. Current applicatio..
Tensile Strength, Ultimate	22.0 MPa	3190 psi
BASF Lucalen® A 2920 M Ethylene/Acrylate Copolymer Used in the manufacture of economical composite films of Lucalen and PE-LD, and as a primer for aluminum steel composites.Data was collected by ISO methods and provided by BASF.
Tensile Strength, Ultimate	22.0 MPa	3190 psi
BASF Lucalen® A 2910 M Ethylene/Acrylate Copolymer For coating metals such as aluminum and steel, and as a primer for composites of metal or paper with Lupolen. Contains an antioxidant.Data was collected by ISO methods and provided by BASF.
Tensile Strength, Ultimate	22.0 MPa	3190 psi	DIN 53455
Ineos Nova S-3201 Medium Impact Compact Polystyrene (discontinued **) Extremely easy flowing medium impact polystyrene, designed for extreme short cycle times for injection molding of household, packaging and toys. The material is provided with external lubricant to ..
Tensile Strength, Ultimate	22.0 - 90.0 MPa	3190 - 13100 psi	Average value: 45.3 MPa Grade Count:27
Overview of materials for Polyethylene Terephthalate (PET), Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Unreinforced". Each property range of values reported is minimum and m..
Tensile Strength, Ultimate	22.0 - 200 MPa	3190 - 29000 psi	Average value: 62.0 MPa Grade Count:104
Overview of materials for Nylon 6, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Impact Grade". Each property range of values reported is minimum and maximum values of appropri..
Tensile Strength, Ultimate	22.0 MPa	3190 psi	ASTM D638
Elastomer Engineering Elastamide 400 Elastomer Modified RIM Nylon 6 18% crystallinity. Information supplied by Elastomer Engineering.
Tensile Strength, Ultimate	22.0 - 115 MPa	3190 - 16700 psi	Average value: 60.9 MPa Grade Count:150